| Texto completo | |
| Autor(es): |
Freitas, Renato Garcia
[1]
;
Batista, Eveline Cristine
[2]
;
Castro, Marcela Portes
[2]
;
Oliveira, Robson T. S.
[2]
;
Santos, Mauro Coelho
[3]
;
Pereira, Ernesto Chaves
[1]
Número total de Autores: 6
|
| Afiliação do(s) autor(es): | [1] Univ Fed Sao Carlos, Dept Quim, LIEC, Ctr Multidisciplinar Desenvolvimento Mat Ceram, BR-13565905 Sao Carlos, SP - Brazil
[2] Univ Fed Vales Jequitinhonha & Mucuri, Fac Ciencias Exatas & Tecnol, Lab Eletroquim, Diamantina, MG - Brazil
[3] Univ Fed Abc, CCNH, LEMN, BR-09210170 Santo Andre, SP - Brazil
Número total de Afiliações: 3
|
| Tipo de documento: | Artigo Científico |
| Fonte: | ELECTROCATALYSIS; v. 2, n. 3, p. 224-230, SEP 2011. |
| Citações Web of Science: | 4 |
| Resumo | |
Bismuth submonolayers covering polycrystalline platinum-surface electrodes have been prepared with several degrees of Bi covering 0.34, 0.58, and 0.92 monolayers, respectively. These samples were used to investigate ethanol electrooxidation using cyclic voltammetry, chronoamperometry, and electrochemical impedance spectroscopy. Suppression of hydrogen adsorption was observed as the degree of Bi covering on the Pt surface increased. Ethanol electrooxidation increased 5.5-fold for Pt/Bi-0.34ML compared with Pt using constant potential polarization at 0.5 V. Electrochemical impedance experiments showed that Pt/Bi-0.34ML electrodes exhibited the lowest charge transfer resistance, which is in agreement with voltammetric and chronoamperometric measurements. (AU) | |
| Processo FAPESP: | 10/05555-2 - Investigação da formação eletroquímica de nanotubos-TiO2 e sua aplicação em sistemas conversores de energia nanoarquiteturados |
| Beneficiário: | Renato Garcia de Freitas Sobrinho |
| Modalidade de apoio: | Bolsas no Brasil - Pós-Doutorado |
| Processo FAPESP: | 03/09933-8 - Núcleo de Excelência em Materiais Nanoestruturados Fabricados Eletroquimicamente |
| Beneficiário: | Ernesto Chaves Pereira de Souza |
| Modalidade de apoio: | Auxílio à Pesquisa - Programa PRONEX - Temático |