Diamagnetism and structural transition in the Ba2Cu3O4Cl2 compound

Autor(es)

M. S. da Luz ^[1] ; C. A. M. dos Santos ^[2] ; A. J. S. Machado ^[3] ; B. Ferreira ^[4]

Afiliação do(s) autor(es)

^[1] FAENQUIL. Departamento de Engenharia de Materiais. Grupo de Supercondutividade - Brasil

^[2] FAENQUIL. Departamento de Engenharia de Materiais. Grupo de Supercondutividade - Brasil

^[3] FAENQUIL. Departamento de Engenharia de Materiais. Grupo de Supercondutividade - Brasil

^[4] FAENQUIL. Departamento de Engenharia de Materiais. Grupo de Supercondutividade - Brasil

• Tipo de documento: Artigo Científico
• Fonte: Brazilian Journal of Physics; v. 32, n. 3, p. 744-747, 2002-09-00.

Resumo

This work presents a study of structural and magnetic properties of the Ba2Cu3O4Cl2 (Ba2342) compound. Doped samples with K or Sr in the Ba site and Zn or Mg in the Cu site of the Ba2342 were prepared using a solid state diffusion method. They were characterized by X-ray powder diffractometry, scanning electron microscopy and dc-magnetization. Samples with Ba2342 composition presented tetragonal structure of the I4/mmm space group when heat-treated at 750ºC. A structural transition was observed when the samples were doped with Zn or Mg or heat-treated at 700ºC. dc-Magnetization measurements performed in SQUID showed the existence of diamagnetic signal. A difference of the magnetic moments measured at zero field cooled (ZFC) and field-cooled (FC) procedures was observed suggesting the existence of localized superconductivity in this oxychloride system. (AU)

• Processo FAPESP: 00/08972-1 - Influência da dopagem com K sobre o composto (Sr,Ba)2Cu3O4Cl2
• Beneficiário: Mário Sérgio da Luz
• Modalidade de apoio: Bolsas no Brasil - Iniciação Científica
• Processo FAPESP: 00/03610-4 - Medidas de efeito Hall em amostras policristalinas do sistema Y(1-X)Pr(X)Ba(2)Cu(3)O(7-gama) próximas da transição supercondutor isolante
• Beneficiário: Carlos Alberto Moreira dos Santos
• Modalidade de apoio: Auxílio à Pesquisa - Regular