Chemical Characterization and Flexural Strength of a Denture Base Acrylic Resin with Monomer 2-Tert-Butylaminoethyl Methacrylate

Texto completo
Autor(es):
Rodriguez, Larissa Santana [1] ; Paleari, Andre Gustavo [1] ; Giro, Gabriela [1] ; de Oliveira Junior, Norberto Martins [1] ; Pero, Ana Carolina [1] ; Compagnoni, Marco Antonio [1]
Número total de Autores: 6
Afiliação do(s) autor(es):
[1] Sao Paulo State Univ, UNESP, Araraquara Dent Sch, Dept Dent Mat & Prosthodont, BR-14801903 Araraquara, SP - Brazil
Número total de Afiliações: 1
Tipo de documento: Artigo Científico
Fonte: JOURNAL OF PROSTHODONTICS-IMPLANT ESTHETIC AND RECONSTRUCTIVE DENTISTRY; v. 22, n. 4, p. 292-297, JUN 2013.
Citações Web of Science: 7
Resumo

Purpose The objectives of this study were to investigate the flexural strength (FS) and chemical interaction between 2-tert-butylaminoethyl methacrylate (TBAEMA) and a denture base acrylic resin. Materials and Methods Specimens were divided into five groups according to the concentration of TBAEMA incorporated in acrylic resin Onda-Cryl (0%, 1%, 2%, 3%, 4%) and were submitted to Fourier transform infrared spectroscopy (FTIR), electron spectroscopy for chemical analysis (XPS-ESCA), and differential scanning calorimetry (DSC) analyses. FS of the specimens was tested, and results were analyzed by ANOVA/Tukey's test ( < 0.05). Results Different nitrogen ratios were observed on specimens' surfaces: 0.36%, 0.54%, 0.35%, and 0.20% for groups 1%, 2%, 3%, and 4%, respectively. FTIR indicated copolymerization of acrylic resin and TBAEMA, and DSC results demonstrated a decrease in glass transition temperature (Tg). Significant differences were found for FS (p < 0.05). The mean values were 91.1 +/- 5.5,A 77.0 +/- 13.1,B 67.2 +/- 12.5,B 64.4 +/- 13.0,B and 67.2 +/- 5.9B MPa for groups 0%, 1%, 2%, 3% and 4%, respectively (same superscript letters indicate no significant difference). Conclusions The incorporation of TBAEMA in acrylic resin resulted in copolymerization and the presence of amine groups on specimens' surfaces, and in decreases of Tg and FS. (AU)