| Texto completo | |
| Autor(es): |
Marcio Andreato Batista Mendes
[1]
;
Ana Karla Melle
[2]
;
Carlos Alberto Caldas de Souza
[3]
;
Claudio Shyinti Kiminami
[4]
;
Régis Daniel Cava
[5]
;
Claudemiro Bolfarini
[6]
;
Walter José Botta Filho
[7]
Número total de Autores: 7
|
| Afiliação do(s) autor(es): | [1] Universidade Federal Tecnológica do Paraná. Departamento de Engenharia de Materiais - Brasil
[2] Universidade Federal de São Carlos. Departamento de Materiais - Brasil
[3] Universidade Federal da Bahia. Departamento de Ciência e Tecnologia dos Materiais - Brasil
[4] Universidade Federal de São Carlos. Departamento de Materiais - Brasil
[5] Universidade Federal de São Carlos. Departamento de Materiais - Brasil
[6] Universidade Federal de São Carlos. Departamento de Materiais - Brasil
[7] Universidade Federal de São Carlos. Departamento de Materiais - Brasil
Número total de Afiliações: 7
|
| Tipo de documento: | Artigo Científico |
| Fonte: | MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS; v. 19, p. 92-96, 2016-10-27. |
| Resumo | |
Based on the Fe60Cr8Nb8B24 alloy, reported in the literature as good Glass Forming Ability (GFA), in this study the GFA of two new compositions was proposed, Fe68-xCrxNb8B24 (x=10,12). They were evaluated as good candidates to be new compositions of Bulk Metallic Glasses (BMG) with better corrosion resistance due to the high Cr content. Rapidly solidified glassy ribbons were processed, and based on their thermal characteristics, the critical thickness of the glassy structure formation (Zc) was estimated. The critical thickness (Zc) obtained experimentally using the wedge-shaped casting method was evaluated and it presented a much lower value than that estimated theoretically. However, the GFA of the compositions analyzed was ranked and this ranking (i.e. whichever has the most or least GFA) is in agreement with the result predicted theoretically. The GFA of Fe58Cr10Nb8B24, which presented a maximum thickness of the amorphous region of wedge-shaped samples of about 0.6 mm (but estimated it would be 3.56 mm), offered good prospects to be a new Fe-based glass former alloy which has better resistance to corrosion than the Fe60Cr8Nb8B24 alloy reported. (AU) | |
| Processo FAPESP: | 13/05987-8 - Processamento e caracterização de ligas metálicas amorfas, metaestáveis e nano-estruturadas |