Understanding perovskite formation through the intramolecular exchange method in ambient conditions

Autor(es)

Szostak, Rodrigo ; Castro, Jhon A. P. ; Marques, Adriano S. ; Nogueira, Ana F.

• Tipo de documento: Artigo Científico
• Fonte: JOURNAL OF PHOTONICS FOR ENERGY; v. 7, n. 2 APR-JUN 2017.
• Citações Web of Science: 6

Resumo

Among the methods to prepare hybrid organic-inorganic perovskite films, the intramolecular exchange method was the first one that made possible to prepare perovskite solar cells with efficiencies higher than 20%. However, perovskite formation by this method is not completely understood, especially in ambient conditions. In this work, perovskite films were prepared by the intramolecular exchange method in ambient conditions. The spin coating speed and the frequency of the MAI solution dripping onto PbI2(DMSO) were varied during the deposition steps. With the combination of these two parameters, a rigid control of the solvent drying was possible. Thus, depending on the chosen conditions, the intermediate (MA)(2)Pb3I8 center dot 2DMSO was formed with residual PbI2. Otherwise, direct formation of perovskite film was attained. A mechanism for the direct formation of bulk perovskite was proposed. We also investigated how the posterior thermal annealing affects the crystallinity and defects in perovskite films. With prolonged thermal annealing, the excess of MAI can be avoided, increasing the efficiency and decreasing the hysteresis of the solar cells. The best perovskite solar cell achieved a stabilized power output of 12.9%. The findings of this work pave the way for realizing the fabrication of efficient perovskite solar cells in ambient atmosphere, a very desirable condition for cost-efficient large scale manufacturing of this technology. (C) 2017 Society of Photo-Optical Instrumentation Engineers (SPIE) (AU)

• Processo FAPESP: 14/13666-0 - Células solares híbridas baseadas em perovskitas
• Beneficiário: Rodrigo Szostak
• Modalidade de apoio: Bolsas no Brasil - Mestrado
• Processo FAPESP: 14/21928-4 - Nanoestruturas híbridas em células solares de terceira geração (3G)
• Beneficiário: Ana Flávia Nogueira
• Modalidade de apoio: Auxílio à Pesquisa - Regular