Antibacterial resin-based composite containing chlorhexidine for dental

Autor(es):Mostrar menos -

Cidreira Boaro, Leticia Cristina ^{[1, 2]} ; Campos, Luiza Mello ^[1] ; Costa Varca, Gustavo Henrique ^[1] ; Ribeiro dos Santos, Tamiris Martins ^[1] ; Marques, Pamela Adeline ^[2] ; Sugii, Mari Miura ^[3] ; Saldanha, Nathalia Ramaldes ^[2] ; Cogo-Muller, Karina ^[3] ; Brandt, William Cunha ^[2] ; Braga, Roberto Ruggiero ^[4] ; Parra, Duclerc F. ^[1]

Afiliação do(s) autor(es)

^[1] CNEN SP, IPEN, BR-05508000 Sao Paulo - Brazil

^[2] Univ Santo Amaro, Fac Odontol, Rua Prof Eneas de Siqueira Neto 340, BR-04829900 Sao Paulo - Brazil

^[3] Univ Estadual Campinas, Fac Odontol, BR-13414903 Sao Paulo - Brazil

^[4] Univ Sao Paulo, Fac Odontol, BR-05508000 Sao Paulo - Brazil

• Tipo de documento: Artigo Científico
• Fonte: Dental Materials; v. 35, n. 6, p. 909-918, JUN 2019.
• Citações Web of Science: 1

Resumo

Objeticve. The aim of this study was to develop a composite material with antibacterial activity using MMT loaded with clorhexidine (CHX). For that it was used a BisGMA/TEGDMA matrix and added low concentration of MMT/CHX. The aim was to evaluate the drug release capacity of MMT, and not to provide reinforcement. Methods. Six experimental composites were made with organic matrix of BisGMA/TEGDMA in equal proportions by weight. The composites received organophlizated montmorillonite with or without CHX. The concentrations were 2,5; 5 or 10% by weight. Degree of conversion (DC) was evaluated using FTIR (peak 6165 cm-1; n = 5). Specimens for flexural properties (10x2x1 mm) were immediate tested (24h). Elastic modulus(E) and flexural strength (FS) was measured using the three point bending test (n = 10). Inibition halo was used to test the antibacterial activity against Staphylococcus aureus, Streptococcus mutans, and Porphyromonas gingivalis (n = 5 for each bacteria). The inhibition of biofilm formation (BF) was evaluated by inserting polymerized disc of composite in to a culture media colonized with Streptococcus mutans (n = 10). The release of CHX was measured using ultraviolet (255 nm) for 10 days (n = 5). The data of degree of conversion was analysed using KruskalWallis/MannWhitney, and the other variables using two-way ANOVA/Tukey, always considering a global level of significance of 5%. Results. DC ranged from 71% to 74%. E ranged from 5.7 to 8.1 GPa. FS ranged from 61.4 to 74.7 MPa. There were no statistical differences among the groups for all the variables. For the three bacteria tested the composites with CHX loaded presented inhibition of growth for all concentration, except for 2,5% that did not inihibited the growth of P. gingivalis. BF was lower for the groups with 10% MMT/CHX, all groups presented BF, even those without CHX loaded. All concentrations presented release off CHX during all the 28 days analyzed. Conclusions. Within the limitation of this study it can be concluded that: all concentrations tested presented release of CHX and reduced BF. All concentration presented antibacterial activity for the three bacteria tested, except for 2,5% that did not inhibit the growth of P. gingivalis. The presence of MMT with CHX loaded did not interfere in the properties evaluated. (C) 2019 The Academy of Dental Materials. Published by Elsevier Inc. All rights reserved. (AU)

• Processo FAPESP: 14/23144-0 - Avaliação da incorporação de clorexidina sobre o grau de conversão de compósitos experimentais utilizando MMT como carga
• Beneficiário: Pâmela Adeline Marques
• Modalidade de apoio: Bolsas no Brasil - Iniciação Científica
• Processo FAPESP: 16/01319-9 - Desenvolvimento de nanocompósitos odontológicos a base de BisGma/TEGDMA com atividade antimicrobiana utilizando nanopartículas de MMT carregadas com clorexidina
• Beneficiário: Letícia Cristina Cidreira Boaro
• Modalidade de apoio: Auxílio à Pesquisa - Regular