Co-doped p-type ZnO:Al-N Thin Films Grown by RF-Magnetron Sputtering at Room Temperature

Autor(es)

Raul Ramos ^[1] ; Marcio Peron Franco de Godoy ^[2] ; Elidiane Cipriano Rangel ^[3] ; Nilson Cristino da Cruz ^[4] ; Steven F. Durrant ^[5] ; José Roberto Ribeiro Bortoleto ^[6]

Afiliação do(s) autor(es)

^[1] Universidade Estadual Paulista. Instituto de Ciência e Tecnologia de Sorocaba - Brasil

^[2] Universidade Federal de São Carlos. Departamento de Física - Brasil

^[3] Universidade Estadual Paulista. Instituto de Ciência e Tecnologia de Sorocaba - Brasil

^[4] Universidade Estadual Paulista. Instituto de Ciência e Tecnologia de Sorocaba - Brasil

^[5] Universidade Estadual Paulista. Instituto de Ciência e Tecnologia de Sorocaba - Brasil

^[6] Universidade Estadual Paulista. Instituto de Ciência e Tecnologia de Sorocaba - Brasil

• Tipo de documento: Artigo Científico
• Fonte: MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS; v. 23, n. 3 2020-08-31.

Resumo

This study reports the structural properties of zinc oxide thin films co-doped with aluminum and nitrogen (ZnO:Al-N) grown by RF magnetron sputtering from an AZO (ZnO with 2 wt% Al2O3) target under nitrogen (N2) atmosphere at room temperature (RT). Nitrogen partial pressures of 0.00, 0.10, 0.25 and 1.00 mTorr were used. The film thickness was around 270 nm. Ultraviolet-Vis-NIR transmittance (T) spectra of the films revealed T values of 80 to 85% in the 400 to 700 nm wavelength range. XRD results indicated that the films had a hexagonal wurtzite structure and were preferentially oriented in the (002) plane. Analyses by EDS indicated that the N atoms tend to be incorporated into the ZnO matrix at the expense of oxygen atoms. The ideal [N]/[Al] was obtained at a N2 partial pressure of 0.25 mTorr, producing a p-type film. For a [N]/[Al] of 1.53, the film also exhibited p-type conduction with an electrical resistivity of 31.92 Ω cm, mobility of 18.65 cm2/V s and carrier density of 1.22 x 1016 cm-3. The low carrier density is attributed to the energetically favorable formation of inactive nitrogen phases instead of acceptor-receiver-acceptor complexes, even at the ideal [N]/[Al]. (AU)