A novel synthesis route to obtain magnetic nanocrystalline cobalt ferrite with photo-Fenton activity

Texto completo
Autor(es):
de Souza, Bruna G. [1, 2] ; Figueira, Gustavo [3] ; Carvalho, Maria H. [4] ; Alcaraz-Gonzalez, Victor [5] ; Saldana-Flores, Karla E. [5] ; Godinho Jr, Mario ; de Oliveira, Adilson J. A. [4] ; Kiminami, Ruth H. G. A. [3] ; Ruotolo, Luis A. M. [2] ; Urquieta-Gonzalez, Ernesto A. [1, 2]
Número total de Autores: 10
Afiliação do(s) autor(es):
[1] Univ Fed Sao Carlos, Res Ctr Adv Mat & Energy, C Postal 676, BR-13565905 Sao Carlos, SP - Brazil
[2] Univ Fed Sao Carlos, Dept Chem Engn, C Postal 676, BR-13565905 Sao Carlos, SP - Brazil
[3] Univ Fed Sao Carlos, Grad Program Mat Sci & Engn, C Postal 676, BR-13565905 Sao Carlos, SP - Brazil
[4] Univ Fed Sao Carlos, Dept Phys, C Postal 676, BR-13565905 Sao Carlos, SP - Brazil
[5] Univ Guadalajara CUCEI, Blvd Marcelino G Barragan 1421, Guadalajara 44430, Jalisco - Mexico
Número total de Afiliações: 5
Tipo de documento: Artigo Científico
Fonte: Materials Chemistry and Physics; v. 257, JAN 1 2021.
Citações Web of Science: 3
Resumo

A novel unconventional coprecipitation procedure (UCP) followed by a simple and fast microwave-assisted hydrothermal (MAH) treatment was used to synthesize a new nanocrystalline magnetic cobalt ferrite (CoFe2O4/MAH) with photo-Fenton activity. The Co-ferrite nanoparticles were obtained at room temperature in the absence of surfactants and their photo-Fenton activity was evaluated through lignin degradation. It was found that microwave hydrothermal treatment is mandatory to obtain magnetic and photoactive Co-ferrite. According to XRD Rietveld refinements and FTIR, the photoactivity was mainly attributed to the Co2+ cation migration from octahedral to tetrahedral sites in the ferrite structure during the MAH treatment, leading, consequently, to a higher Fe3+ incorporation at octahedral sites, which strongly participate in the photo-Fenton degradation mechanism. The magnetic property of the CoFe2O4/MAH ferrite nanoparticles was confirmed by magnetometry and provided an easy catalyst separation. (AU)

Processo FAPESP: 13/07296-2 - CDMF - Centro de Desenvolvimento de Materiais Funcionais
Beneficiário:Elson Longo da Silva
Modalidade de apoio: Auxílio à Pesquisa - Centros de Pesquisa, Inovação e Difusão - CEPIDs
Processo FAPESP: 17/13769-1 - Materiais multiferróicos e ferroelétricos para conversores de energia: síntese, propriedades, fenomenologia e aplicações
Beneficiário:José Antonio Eiras
Modalidade de apoio: Auxílio à Pesquisa - Temático
Processo FAPESP: 17/24995-2 - Magnetismo em materiais multifuncionais
Beneficiário:Adilson Jesus Aparecido de Oliveira
Modalidade de apoio: Auxílio à Pesquisa - Regular
Processo FAPESP: 09/54082-2 - EMU: projeto para aquisição de um magnetômetro de amostra vibrante que utiliza como sensor um dispositivo supercondutor de interferência quântica acoplado (Squid-VSM) com circuito fechado de criogenia
Beneficiário:Ernesto Chaves Pereira de Souza
Modalidade de apoio: Auxílio à Pesquisa - Programa Equipamentos Multiusuários