Y-TZP Physicochemical Properties Conditioned with ZrO2 and SiO2 Nanofilms and Bond Strength to Dual Resin Cement

Texto completo
Autor(es):
Ribeiro, Ricardo Faria ; Oliveira, Danilo Flamini ; Tovani, Camila Bussola ; Ramos, Ana Paula ; Sanches Borges, Ana Flavia ; Lapria Faria, Adriana Claudia ; de Almeida, Rossana Pereira ; Silveira Rodrigues, Renata Cristina
Número total de Autores: 8
Tipo de documento: Artigo Científico
Fonte: MATERIALS; v. 15, n. 22, p. 16-pg., 2022-11-01.
Resumo

Commercial Yttria-tetragonal zirconia polycrystalline (Y-TZP) was subjected to surface treatments, and the bond strength of dual resin cement to Y-TZP and failure modes were evaluated. Disks (12 mm x 2 mm), cylinders (7 mm x 3.3 mm), and bars (25 mm x 5 mm x 2 mm) were milled from Y-TZP CAD-CAM blocks, divided into seven groups, and subjected to different surface treatments; silicatization was used as control. On the basis of the literature, this study evaluated modifications with films containing SiO2 nanoparticles and silane; SiO2+ZrO2-SiO2 (50%) and ZrO2 (50%) nanoparticles, SiO2+ZrO(2/)Silane-SiO2 (50%) and ZrO2 (50%) nanoparticles, and silane. Specimens were analyzed by wettability (n = 3), surface free energy (n = 3), X-ray diffraction (n = 1), Fourier transform infrared spectroscopy (FTIR) (n = 1), roughness (n = 5), shear bond test (n = 10), and dynamic modulus (n = 3). Specimens treated with hydrofluoric acid-HF 40% presented significantly higher contact angle and lowest surface free energy (p < 0.05). The SiO2/Silane presented crystalline SiO2 on the surface. The surface roughness was significantly higher for groups treated with nanofilms (p < 0.05). Shear bond strength was significantly higher for silicatization, HF 40%/silicatization, SiO2/Silane, and SiO2+ZrO2/Silane groups. The proposed treatments with nanofilms had potentially good results without prejudice to the physicochemical characteristics of zirconia. Generally, groups that underwent silica surface deposition and silanization had better bond strength (p < 0.005). (AU)

Processo FAPESP: 14/16977-6 - Caracterização superficial de Y-TZP pós tratamento ácido, silicatização e filme de nanopartículas de Si-ZrO2 e avaliação da adesão pós tratamentos, individuais ou combinados, de coroas/pilares CAD/CAM em simulação de uso e fadiga termomecânica acelerada
Beneficiário:Ricardo Faria Ribeiro
Modalidade de apoio: Auxílio à Pesquisa - Regular