Recycling of carbon fibers inserted in composite of DGEBA epoxy matrix by thermal degradation

Texto completo
Autor(es):
Matielli Rodrigues, Gleice Guevara ; Faulstich de Paiva, Jane Maria ; do Carmo, Janaina Braga ; Botaro, Vagner R.
Número total de Autores: 4
Tipo de documento: Artigo Científico
Fonte: Polymer Degradation and Stability; v. 109, p. 9-pg., 2014-11-01.
Resumo

In this study, carbon fibers inserted into an epoxy resin derived from diglycidyl ether of bisphenol-A (DGEBA) were recovered based on the complete removal of the matrix by thermal treatment. The degradation of the composite was carried out at various experimental conditions and the ideal one was obtained at 450 degrees C for 2 h. Under this condition, all of the resin was removed without degrading the C fibers to any significant degree. The results of thermogravimetric analysis revealed several stages of thermal decomposition depending on the material analyzed. It was established by thermogravimetry analyses that the epoxy matrix starts to experience intense degradation at temperatures above 280 degrees C with maximum loss in the temperature range of 360-410 degrees C. In the case of composite samples above 800 degrees C a residue of approximately 50% by weight can be observed, which is related to carbon fibers. Confirmation of the removal of the resin from the carbon fiber was obtained by means of scanning electron microscopy (SEM) and Fourier Transform Infrared Spectroscopy (FTIR). The kinetic of release of CH4, CO2 and N2O gases during degradation process was accompanied by gas chromatography. The concentrations of methane and carbon dioxide increased significantly during the first 10 min of the processing and after this, no released quantities were verified. On the other hand N2O continues to be released even after 3 h of the process of burning the composite in air atmosphere. The treatment proposed in this study can be considered to be a low-cost one as well as being interesting for the recovery of C fibers present in DGEBA matrix which would normally be discarded after use. (C) 2014 Elsevier Ltd. All rights reserved. (AU)

Processo FAPESP: 09/00855-0 - Estudo do comportamento térmico dinâmico-mecânico de materiais compósitos a base de fibras vegetais modificadas e matriz polimérica
Beneficiário:Vagner Roberto Botaro
Modalidade de apoio: Auxílio à Pesquisa - Jovens Pesquisadores
Processo FAPESP: 06/60885-2 - Moldagem de compósitos poliméricos reforçados com mantas de fibras vegetais e estudo de duas propriedades térmicas e dinâmico mecânicas
Beneficiário:Jane Maria Faulstich de Paiva
Modalidade de apoio: Auxílio à Pesquisa - Jovens Pesquisadores
Processo FAPESP: 08/55989-9 - Emissões de óxido nitroso (N2O), dióxido de carbono (CO2) e metano (CH4) a partir de solos cultivados com cana-de-açúcar no estado de São Paulo, Brasil
Beneficiário:Janaina Braga do Carmo
Modalidade de apoio: Auxílio à Pesquisa - Programa BIOEN - Jovens Pesquisadores