Characterization of NiTiNb10.5 shape memory alloy: microstructural aspects and high-temperature oxidation behavior

Autor(es)

Martins Junior, C. B. ; Silva, R. ; Gargarella, P. ; Gleeson, B. ; Rovere, C. A. D.

• Tipo de documento: Artigo Científico
• Fonte: Corrosion Science; v. 225, p. 12-pg., 2023-10-31.

Resumo

The influence of Niobium addition on the high-temperature oxidation behavior of NiTi shape-memory alloys was investigated. Mass-gain kinetics were determined for up to 100 h oxidation at 800, 900 and 1000 degrees C. Niobium addition drastically reduced the oxidation rates. The surface and cross-section of the resulting oxide layers were characterized by XRD and SEM/EDS. The presence of Nb changed the morphology, phase assemblage, and composition of the scale product, which directly influenced the observed results. The postulated reasons for the improved oxidation resistance were the Nb-doping of TiO2 and the formation of an Nb-rich layer at the scale/ alloy interface. (AU)

• Processo FAPESP: 17/27031-4 - Influência de parâmetros de processo nas características metalúrgicas de peças fabricadas por manufatura aditiva
• Beneficiário: Piter Gargarella
• Modalidade de apoio: Auxílio à Pesquisa - Jovens Pesquisadores
• Processo FAPESP: 22/03139-9 - Design e produção de ligas multicomponentes refratárias com propriedades otimizadas de oxidação em alta temperatura
• Beneficiário: Carlos Alberto Della Rovere
• Modalidade de apoio: Auxílio à Pesquisa - Projeto Inicial
• Processo FAPESP: 19/23610-5 - Comportamento de oxidação em temperaturas elevadas de ligas NiTiNb com efeito memória de forma
• Beneficiário: Claudio Beserra Martins Júnior
• Modalidade de apoio: Bolsas no Brasil - Mestrado