Synthesis and characterization of hybrid composites based on carbon nanotubes

Texto completo
Autor(es):
Canobre, Sheila C. [1] ; Almeida, Dalva A. L. [1] ; Fonseca, Carla Polo [1] ; Neves, Silmara [1]
Número total de Autores: 4
Afiliação do(s) autor(es):
[1] Univ San Francisco, Programa Posgrad Engn & Ciencia Mat, LCAM, BR-13251900 Itatiba, SP - Brazil
Número total de Afiliações: 1
Tipo de documento: Artigo Científico
Fonte: Electrochimica Acta; v. 54, n. 26, p. 6383-6388, NOV 1 2009.
Citações Web of Science: 33
Resumo

Multi-wall carbon nanotubes (CNTs) were coated with protonated polyaniline (PAni) in situ during the chemical polymerization of aniline. Uniform coating of CNT with PAni was observed by scanning electronic microscopy. An improvement in the covering of CNT composites was found by the association of poly(2,5-dimercapto-1,3,4-thiadiazole) (PDMcT). The conductivity of composites has been compared with the conductivity of the PAni and CNT. A maximum conductivity of 96.8 S cm(-1) has been found for a PAni/PDMcT/CNT composite. High capacitance value (289.4 F g(-1)) was also determined for this composite, indicating that all materials, PAni, PDMcT and CHT, remain active during the charge-discharge cycling. The reduction in the capacitance after 100 cycles was found to be less than 25%. The capacitive behavior of all materials was confirmed by impedance analysis. (c) 2009 Elsevier Ltd. All rights reserved. (AU)

Processo FAPESP: 06/50967-1 - Sintese e caracterizacao de compositos polimericos obtidos via template.
Beneficiário:Silmara das Neves
Modalidade de apoio: Auxílio à Pesquisa - Regular
Processo FAPESP: 05/54578-7 - Desenvolvimento e aplicacao de compositos de polimeros condutores obtidos via sintese template.
Beneficiário:Sheila Cristina Canobre
Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado