Abutment Design for Implant-Supported Indirect Composite Molar Crowns: Reliability and Fractography

Autor(es)

Bonfante, Estevam Augusto ^[1] ; Suzuki, Marcelo ^[2] ; Lubelski, William ^[3] ; Thompson, Van P. ^[4] ; de Carvalho, Ricardo Marins ^[5] ; Witek, Lukasz ^[4] ; Coelho, Paulo G. ^{[4, 6]}

Afiliação do(s) autor(es)

^[1] UNIGRANRIO Univ, Sch Hlth Sci, Postgrad Program Dent, Duque De Caxias, RJ - Brazil

^[2] Tufts Univ, Sch Dent Med, Dept Prosthodont, Boston, MA 02111 - USA

^[3] Bicon Dent Implant Ctr, Dept Engn & Res, Boston, MA - USA

^[4] NYU, Coll Dent, Dept Biomat & Biomimet, New York, NY - USA

^[5] Univ British Columbia, Fac Dent, Div Biomat, Dept Oral Biol & Med Sci, Vancouver, BC V5Z 1M9 - Canada

^[6] NYU, Coll Dent, Dept Periodontol & Implant Dent, New York, NY - USA

• Tipo de documento: Artigo Científico
• Fonte: JOURNAL OF PROSTHODONTICS-IMPLANT ESTHETIC AND RECONSTRUCTIVE DENTISTRY; v. 21, n. 8, p. 596-603, DEC 2012.
• Citações Web of Science: 10

Resumo

Purpose: To investigate the reliability of titanium abutments veneered with indirect composites for implant-supported crowns and the possibility to trace back the fracture origin by qualitative fractographic analysis. Materials and Methods: Large base (LB) (6.4-mm diameter base, with a 4-mm high cone in the center for composite retention), small base (SB-4) (5.2-mm base, 4-mm high cone), and small base with cone shortened to 2 mm (SB-2) Ti abutments were used. Each abutment received incremental layers of indirect resin composite until completing the anatomy of a maxillary molar crown. Step-stress accelerated-life fatigue testing (n = 18 each) was performed in water. Weibull curves with use stress of 200 N for 50,000 and 100,000 cycles were calculated. Probability Weibull plots examined the differences between groups. Specimens were inspected in light-polarized and scanning electron microscopes for fractographic analysis. Results: Use level probability Weibull plots showed Beta values of 0.27 for LB, 0.32 for SB-4, and 0.26 for SB-2, indicating that failures were not influenced by fatigue and damage accumulation. The data replotted as Weibull distribution showed no significant difference in the characteristic strengths between LB (794 N) and SB-4 abutments (836 N), which were both significantly higher than SB-2 (601 N). Failure mode was cohesive within the composite for all groups. Fractographic markings showed that failures initiated at the indentation area and propagated toward the margins of cohesively failed composite. Conclusions: Reliability was not influenced by abutment design. Qualitative fractographic analysis of the failed indirect composite was feasible. (AU)

• Processo FAPESP: 10/06152-9 - Confiabilidade e modos de fratura de próteses fixas em compósitos indiretos com e sem infra-estrutura CAD/CAM sobre implantes