Effect of Various Aging Protocols and Intermediate Agents on the Bond Strength of Repaired Composites

Autor(es)

Silva Sousa, Ana Beatriz ^[1] ; Jardilino Silami, Francisca Daniele ^[1] ; Roberti Garcia, Lucas da Fonseca ^[1] ; Naves, Lucas Zago ^[2] ; Panzeri Pires-de-Souza, Fernanda de Carvalho ^[1]

Afiliação do(s) autor(es)

^[1] Univ Sao Paulo, Ribeirao Preto Sch Dent, BR-14040904 Ribeirao Preto, SP - Brazil

^[2] Univ Estadual Campinas, Piracicaba Sch Dent, Piracicaba, SP - Brazil

• Tipo de documento: Artigo Científico
• Fonte: Journal of Adhesive Dentistry; v. 15, n. 2, p. 137-144, 2013.
• Citações Web of Science: 7

Resumo

Purpose: To evaluate the effect of two adhesive systems and different aging protocols on the bond strength of a repaired microhybrid composite. Materials and Methods: Eighty test specimens (n = 20) and 10 control specimens measuring 8 x 4 mm were fabricated of a microhybrid composite (4 Seasons, shade A2) and grouped according to time/aging protocol: G1: 24 h in artificial saliva; G2: 7 days in artificial saliva; G3: 30 days in artificial saliva; G4: artificial accelerated aging (AAA) for 384 h; G5: control. After aging, samples were submitted to three types of surface treatment: SB2: Adper Single Bond 2, a two-step adhesive (3M ESPE); SB3: Adper Scotchbond Multi-Purpose, a three-step adhesive (3M ESPE); C: without application of adhesive (control). After this, test specimens were repaired with the same composite of a different shade (C3), and submitted to the microtensile test at a crosshead speed of 0.5 mm/min. Failure modes were analyzed by scanning electron microscopy (Jeol JSM 7500). Statistical analysis was performed using ANOVA and Tukey's test (p < 0.05). Results: G2/SB2 presented significantly lower bond strength values in comparison with the other groups (p < 0.05). The control group presented the highest bond strength values, which differed statistically significantly from SB3, G3/SB2, and G4/SB2 (p < 0.05). Fractographic analysis demonstrated that most samples presented predominantly cohesive failures, excepting GI/SB2, which presented mixed and cohesive failures, and G4/SB2 and G1/SB3, which showed adhesive failures. Conclusion: The repair was more effective when performed after a short period of time and when the 3-step adhesive system (SB3) was used. (AU)