Dielectric dispersion in Bi3Zn2Sb3O14 ceramic: a pyrochlore type phase

Autor(es)

Silvania Lanfredi ^[1] ; Marcos A. de Lima Nobre ^[2]

Afiliação do(s) autor(es)

^[1] Universidade de São Paulo. Instituto de Física de São Carlos - Brasil

^[2] Universidade de São Paulo. Instituto de Física de São Carlos - Brasil

• Tipo de documento: Artigo Científico
• Fonte: MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS; v. 6, n. 2, p. 157-161, 2003-06-00.

Resumo

The electric and dielectric properties of Bi3Zn2Sb3O14 ceramic were studied by impedance spectroscopy. The measurements were performed in the frequency range 5 to 13 MHz and at temperature ranges from 25 to 700 °C. The permittivity was calculated by the variation of the imaginary part of the impedance (-Im(Z)) as function of 1/omega, where omega represents the angular frequency (2pif). The parameter epsilon = f(T) exhibits values in the range from 40 to 48. The dielectric losses (tandelta) show slight dependence with the temperature up to 400 °C. A strong increasing of the tandeltaoccurs at temperatures higher than 400 °C. In a general way, a decrease of the parameter tandelta occurs with the increasing frequency. (AU)

• Processo FAPESP: 01/13421-7 - Cerâmicas e filmes dielétricos de óxidos semicondutores ferroelétricos nanoestruturados da família tetragonal tungstênio bronze: processamento, caracterização e propriedades
• Beneficiário: Silvania Lanfredi
• Modalidade de apoio: Auxílio à Pesquisa - Jovens Pesquisadores
• Processo FAPESP: 97/04760-5 - Estudo das propriedades eletricas de niobatos alcalinos e algumas de suas solucoes solidas.
• Beneficiário: Silvania Lanfredi
• Modalidade de apoio: Bolsas no Brasil - Doutorado
• Processo FAPESP: 99/03749-3 - PREPARACAO DE MEMBRANAS CERAMICAS A BASE DE A12O3 REFORCADAS COM SiC.
• Beneficiário: Marcos Augusto de Lima Nobre
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado