Physical, chemical, and biological properties of white MTA with additions of AlF3

Autor(es)

Marciano, Marina Angelica ^[1] ; Camilleri, Josette ^[2] ; Lucateli, Ribamar Lazanha ^[3] ; Costa, Reginaldo Mendonca ^[4] ; Matsumoto, Mariza Akemi ^[5] ; Hungaro Duarte, Marco Antonio ^[4]

Afiliação do(s) autor(es)

^[1] Univ Campinas UNICAMP, Dent Sch Piracicaba, Dept Restorat Dent, Piracicaba, SP - Brazil

^[2] Univ Birmingham, Sch Dent, Birmingham, W Midlands - England

^[3] Univ Sao Paulo, Dent Sch Ribeirao Preto, Dept Surg & Periodontol, Ribeirao Preto, SP - Brazil

^[4] Univ Sao Paulo, Dent Sch Bauru, Dept Dent Endodont & Dent Mat, Bauru, SP - Brazil

^[5] State Univ Sao Paulo UNESP, Dent Sch Aracatuba, Dept Morphol, Aracatuba, SP - Brazil

• Tipo de documento: Artigo Científico
• Fonte: CLINICAL ORAL INVESTIGATIONS; v. 23, n. 1, p. 33-41, JAN 2019.
• Citações Web of Science: 2

Resumo

ObjectivesAddition of aluminum fluoride (AlF3) to MTA was tested to inhibit dental discoloration.Materials and methodsMTA Angelus with 0, 5, 15, and 45% AlF3 were tested. The set cements were characterized using scanning electron microscopy, energy-dispersive spectroscopy, and X-ray diffraction. Radiopacity and setting time were analyzed according to ANSI/ADA 57 and ASTM C266-08. Volume change was evaluated using volumetric micro-CT analysis. The pH and calcium ion release were assessed after 3 and 24h and 28days. Dental discoloration in contact with the cements was assessed after 24h and 28 and 90days of contact with bovine and human dentine. Tissue reaction to subcutaneous implantation in rats was examined after 30 and 60days.ResultsAlF(3) altered the microstructure of MTA. The addition of 5% AlF3 did not significantly alter the radiopacity, setting time, and volume change (p>0.05). pH and calcium ion release significantly increased with addition of AlF3 (p>0.05). All the tested proportions of AlF3 prevented the dental darkening verified for MTA Angelus in bovine and human teeth. AlF3 did not interfere in inflammatory response of MTA in all periods of analysis; otherwise, lower amounts showed less intense inflammatory infiltrate.Clinical relevanceAlF(3) prevents destabilization of bismuth oxide and consequent tooth darkening, frequently verified in clinical practice when using white MTA.ConclusionsThe use of 5% of AlF3 in combination to MTA resulted in a cement that did not result in dental discoloration and did not affect significantly physical, chemical, and biological properties. (AU)

• Processo FAPESP: 14/01003-6 - Adição de cloreto de alumínio e fluoreto de alumínio para inibir a descoloração dentária ocasionada pelo MTA: avaliação das propriedades físicas, químicas e biológicas
• Beneficiário: Marina Angélica Marciano da Silva
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado
• Processo FAPESP: 17/05096-7 - Avaliação das propriedades físicas, químicas e antimicrobianas de um novo cimento reparador de alta plasticidade
• Beneficiário: Marina Angélica Marciano da Silva
• Modalidade de apoio: Auxílio à Pesquisa - Regular