Galvanic and asymmetry effects on the local electrochemical behavior of the 2098-T351 alloy welded by friction stir welding

Autor(es)

Milagre, Mariana X. ^[1] ; Donatus, Uyime ^[1] ; Mogili, V, Naga ; Silva, Rejane Maria P. ^[1] ; de Viveiros, Barbara Victoria G. ^[1] ; Pereira, Victor F. ^[2] ; Antunes, Renato A. ^[3] ; Machado, Caruline S. C. ^[1] ; Araujo, Joao Victor S. ^[1] ; Costa, Isolda ^[1]

Afiliação do(s) autor(es)

^[1] CNEN, IPEN, Av Prof Lineu Prestes 2242, Sao Paulo - Brazil

^[2] Mogili, Naga, V, LNNano CNPEN, Lab Nacl Nanotecnol, Rua Giuseppe Maximo Scolfaro 10-000, Campinas - Brazil

^[3] Univ Fed Abc, Ctr Engn Modelagem & Ciencias Sociais Aplicadas, Av Estados 5001, Santo Andre, SP - Brazil

• Tipo de documento: Artigo Científico
• Fonte: JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY; v. 45, p. 162-175, MAY 15 2020.
• Citações Web of Science: 3

Resumo

Scanning electrochemical microscopy (SECM) and scanning vibrating electrode technique (SVET) were used to investigate the electrochemical behaviour of the top surface of the 2098-T351 alloy welded by friction stir welding (FSW). The SVET technique was efficient in identifying the cathodic and anodic weld regions. The welding joint (WJ), which comprises the thermomechanically affected zone (TMAZ) and the stir zone (SZ), was cathodic relative to the heated affected zone (HAZ) and the base metal (BM). The reactivities of the welding joint at the advancing side (AS) and the retreating side (RS) were analyzed and compared using SECM technique in the competition mode by monitoring the dissolved oxygen as a redox mediator in 0.005 mol L-1 NaCl solution. The RS was more electrochemically active than the AS, and these results were correlated with the microstructural features of the welded alloy. (C) 2020 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science \& Technology. (AU)

• Processo FAPESP: 13/13235-6 - Estudo da corrosão localizada e caracterização da resistência à corrosão associada à fadiga na região de solda em ligas de alumínio de elevada resistência soldadas por fricção (FSW)
• Beneficiário: Isolda Costa
• Modalidade de apoio: Auxílio à Pesquisa - Temático
• Processo FAPESP: 18/06880-6 - Utilização de técnicas eletroquímicas localizadas para estudo da corrosão de ligas de alumínio de elevada resistência mecânica soldadas por fricção (FSW).
• Beneficiário: Rejane Maria Pereira da Silva
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado
• Processo FAPESP: 17/03095-3 - Investigação da suscetibilidade à corrosão de ligas Al-Cu-Li com solda por atrito (FSW) utilizando a técnica de varredura do eletrodo vibratório (SVET)
• Beneficiário: Uyime Donatus
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado