Equilibrium, Thermodynamic, Reuse, and Selectivity Studies for the Bioadsorption of Lanthanum onto Sericin/Alginate/Poly(vinyl alcohol) Particles

Autor(es)

da Costa, Talles Barcelos ^[1] ; da Silva, Meuris Gurgel Carlos ^[1] ; Vieira, Melissa Gurgel Adeodato ^[1]

Afiliação do(s) autor(es)

^[1] Univ Estadual Campinas, Sch Chem Engn, Albert Einstein Ave, BR-13083852 Campinas - Brazil

• Tipo de documento: Artigo Científico
• Fonte: POLYMERS; v. 13, n. 4 FEB 2021.
• Citações Web of Science: 0

Resumo

In a scenario of high demand, low availability, and high economic value, the recovery of rare-earth metals from wastewater is economically and environmentally attractive. Bioadsorption is a promising method as it offers simple design and operation. The aim of this study was to investigate lanthanum bioadsorption using a polymeric bioadsorbent of sericin/alginate/poly(vinyl alcohol)-based biocomposite. Batch system assays were performed to evaluate the equilibrium, thermodynamics, regeneration, and selectivity of bioadsorption. The maximum capture amount of lanthanum at equilibrium was 0.644 mmol/g at 328 K. The experimental equilibrium data were better fitted by Langmuir and Dubinin-Radushkevich isotherms. Ion exchange mechanism between calcium and lanthanum (2:3 ratio) was confirmed by bioadsorption isotherms. Thermodynamic quantities showed that the process of lanthanum bioadsorption was spontaneous (-17.586, -19.244, and -20.902 kJ/mol), endothermic (+15.372 kJ/mol), and governed by entropic changes (+110.543 J/mol center dot K). The reusability of particles was achieved using 0.1 mol/L HNO3/Ca(NO3)(2) solution for up to five regeneration cycles. The bioadsorbent selectivity followed the order of lanthanum > cadmium > zinc > nickel. Additionally, characterization of the biocomposite prior to and post lanthanum bioadsorption showed low porosity (9.95 and 12.35%), low specific surface area (0.054 and 0.019 m(2)/g), amorphous character, and thermal stability at temperatures up to 473 K. This study shows that sericin/ alginate/poly(vinyl alcohol)-based biocomposites are effective in the removal and recovery of lanthanum from water. (AU)

• Processo FAPESP: 17/18236-1 - Recuperação de íons metálicos nobres e íons terras-raras presentes em soluções aquosas por bioadsorção em partículas de blenda de sericina e alginato
• Beneficiário: Melissa Gurgel Adeodato Vieira
• Modalidade de apoio: Auxílio à Pesquisa - Regular
• Processo FAPESP: 19/11353-8 - Centro Brasileiro de Pesquisa em Água (BWRC)
• Beneficiário: Lauro Tatsuo Kubota
• Modalidade de apoio: Auxílio à Pesquisa - Programa Centros de Pesquisa em Engenharia