Influence of chloride ions concentration on the development of severe localised corrosion and its effects on the electrochemical response of the 2198-T8 alloy

Autor(es)

Carvalho Machado, Caruline de Souza ^[1] ; Pereira da Silva, Rejane Maria ^[1] ; de Sousa Araujo, Joao Victor ^[1] ; Milagre, Mariana Xavier ^[1] ; Donatus, Uyime ^[1] ; Goncalves de Viveiros, Barbara Victoria ^[1] ; Klumpp, Rafael Emil ^[1] ; Costa, Isolda ^[1]

Afiliação do(s) autor(es)

^[1] Nucl & Energy Res Inst IPEN CNEN, Mat Sci & Technol Ctr, Sao Paulo - Brazil

• Tipo de documento: Artigo Científico
• Fonte: CORROSION ENGINEERING SCIENCE AND TECHNOLOGY; v. 56, n. 4, p. 341-350, MAY 19 2021.
• Citações Web of Science: 0

Resumo

The development of severe localised corrosion (SLC) on the 2198-T8 alloy was investigated in solutions of various NaCl concentrations (0.001, 0.005 and 0.01 mol L-1). Immersion tests, optical profilometry, conventional and local electrochemical analyses were performed to evaluate the corrosion behaviour of the alloy. Immersion tests showed that the alloy is susceptible to SLC in all conditions, although the pits sizes were dependent on the solution concentration. The largest anodic areas, corresponding to SLC sites, were observed for the sample immersed in 0.001 mol L-1 NaCl, whereas pits with similar sizes were observed for the samples immersed in solutions with 0.005 and 0.01 mol L-1 of NaCl. Moreover, the maximum depth of attack was observed for the sample immersed in 0.001 mol L-1 NaCl. These results were in agreement with the scanning ion-selective electrode technique (SIET) maps which showed stronger acidification on the sample exposed to 0.001 mol L-1 NaCl solution. (AU)

• Processo FAPESP: 18/06880-6 - Utilização de técnicas eletroquímicas localizadas para estudo da corrosão de ligas de alumínio de elevada resistência mecânica soldadas por fricção (FSW).
• Beneficiário: Rejane Maria Pereira da Silva
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado
• Processo FAPESP: 13/13235-6 - Estudo da corrosão localizada e caracterização da resistência à corrosão associada à fadiga na região de solda em ligas de alumínio de elevada resistência soldadas por fricção (FSW)
• Beneficiário: Isolda Costa
• Modalidade de apoio: Auxílio à Pesquisa - Temático
• Processo FAPESP: 17/03095-3 - Investigação da suscetibilidade à corrosão de ligas Al-Cu-Li com solda por atrito (FSW) utilizando a técnica de varredura do eletrodo vibratório (SVET)
• Beneficiário: Uyime Donatus
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado