Comparative Study of Different Methods for the Preparation of CoxOy/C for the Electrosynthesis of Hydrogen Peroxide

Autor(es)

Assumpcao, M. H. M. T. ^[1] ; Rascio, D. C. ^[1] ; Ladeia, J. P. B. ^[1] ; De Souza, R. F. B. ^[1] ; Neto, E. Teixeira ^[1] ; Calegaro, M. L. ^[2] ; Oliveira, R. T. S. ^[3] ; Gaubeur, I. ^[1] ; Lanza, M. R. V. ^[2] ; Santos, M. C. ^[1]

Afiliação do(s) autor(es)

^[1] UF ABC, LEMN, CCNH, BR-09210170 Santo Andre, SP - Brazil

^[2] USP, IQSC, BR-13566590 Sao Carlos, SP - Brazil

^[3] Fac Ciencias Exatas & Sociais Aplicadas, Diamantina, MG - Brazil

• Tipo de documento: Artigo Científico
• Fonte: International Journal of Electrochemical Science; v. 6, n. 5, p. 1586-1596, MAY 2011.
• Citações Web of Science: 13

Resumo

A comparative study of the sol-gel method (SGM) and polymeric precursor method (PPM) for the synthesis of CoxOy/C electrocatalysts has been performed. CoxOy/C electrocatalysts can electrogenerate hydrogen peroxide (H(2)O(2)), which is desirable for the electrochemical treatment of effluent containing organic pollutants in aqueous or non-aqueous medium. The results showed that SGM was superior for the synthesis of CoxOy/C catalysts for H(2)O(2) electrogeneration. Analysis of Xray diffraction for CoxOy/C prepared by PPM identified only one phase comprising Co(3)O(4). Besides for CoxOy/C prepared by SGM a mixture of oxides was observed: CoO and Co(2)O(4). The average size of crystallites in this material was 5 nm. A rotating ring-disc electrode was used for electrochemical analysis of the oxygen reduction reaction (ORR). The results showed that the SGM was better than PPM for H(2)O(2) electrogeneration since it showed the highest ring-currents. Results also indicate that the number of electrons transferred in the ORR for SGM and PPM were 2.4 and 3.5, while the percentage of H(2)O(2) formed was 78 % and 23 %, respectively. The results were obtained in a 1 M NaOH and 1 M H(2)SO(4) electrolytes. CoxOy/C synthesized with SGM is a promising material for the production of H(2)O(2). (AU)

• Processo FAPESP: 05/59992-6 - Materiais nanoestruturados: eletrocatálise e membranas de óxidos
• Beneficiário: Mauro Coelho dos Santos
• Modalidade de apoio: Auxílio à Pesquisa - Jovens Pesquisadores
• Processo FAPESP: 08/58789-0 - Eletrocatalise da reação de redução de oxigênio utilizando-se catalisadores binários baseados em Pt
• Beneficiário: Daniel Campana Rascio
• Modalidade de apoio: Bolsas no Brasil - Iniciação Científica
• Processo FAPESP: 07/04759-0 - ESTUDO DE ELETRODOS DE DIFUSÃO GASOSA (EDG) MODIFICADOS COM CATALISADORES ORGANOMETÁLICOS PARA A ELETROGERAÇÃO DE H2O2 in situ
• Beneficiário: Marcos Roberto de Vasconcelos Lanza
• Modalidade de apoio: Auxílio à Pesquisa - Regular
• Processo FAPESP: 09/09145-6 - Estudo do mecanismo de oxidação eletroquímica de etanol com eletrocatalisadores de PtSn, PtCe e PtSnCe utilizando técnicas espectroscópicas in-situ
• Beneficiário: Rodrigo Fernando Brambilla de Souza
• Modalidade de apoio: Bolsas no Brasil - Doutorado
• Processo FAPESP: 10/04539-3 - Síntese e caracterização de eletrocatalisadores nanoestruturados para obtenção de peróxido de hidrogênio in situ e posterior degradação de poluentes orgânicos
• Beneficiário: Mônica Helena Marcon Teixeira Assumpção
• Modalidade de apoio: Bolsas no Brasil - Doutorado Direto