CO2-lased enamel microhardness after brushing and cariogenic challenge

Texto completo
Autor(es):
Correa-Afonso, Alessandra Marques [1] ; Bachmann, Luciano [2] ; de Almeida, Cintia Guimaraes [1] ; Palma Dibb, Regina Guenka [3] ; Milori Corona, Silmara Aparecida [3] ; Borsatto, Maria Cristina [1]
Número total de Autores: 6
Afiliação do(s) autor(es):
[1] Univ Sao Paulo, Fac Odontol Ribeirao Preto, Dept Clin Infantil, BR-14040904 Ribeirao Preto, SP - Brazil
[2] Univ Sao Paulo, Fac Filosofia Ciencias & Letras Ribeirao Preto, Dept Fis, BR-14040901 Ribeirao Preto, SP - Brazil
[3] Univ Sao Paulo, Fac Odontol Ribeirao Preto, Dept Odontol Restauradora, BR-14040904 Ribeirao Preto, SP - Brazil
Número total de Afiliações: 3
Tipo de documento: Artigo Científico
Fonte: Journal of Biomedical Optics; v. 18, n. 10 OCT 2013.
Citações Web of Science: 0
Resumo

This study aimed to assess how the wear that brushing promotes affects CO2 laser-irradiated enamel microhardness after cariogenic challenge in vitro. Forty fragments measuring 4 x 4 mm were randomly assigned to four groups according to the enamel surface treatment: G1-control, G2-CO2-laser irradiation, G3-brushing, and G4-CO2 laser irradiation + brushing. A laser device emitting at 10.6 mu m was used (power 0.5 W, energy per pulse 0.05 mJ, and frequency 10 kHz). Specimens belonging to groups G3 and G4 were brushed (80,000 strokes) with a brushing simulator using toothpaste. Next, the samples were challenged with acid: the specimens were immersed in demineralizing and remineralizing solutions for 8 days. The acid resistance of enamel was evaluated by cross-sectional microhardness tests. The area under the curve (KHN x mu m) was calculated. Analysis of variance (ANOVA) one-away and Fisher's test were performed for the statistical analysis (p < 0.05). Group G2 specimens (31; 185 +/- 4706) were statistically different from specimens belonging to groups G1 (26; 723 +/- 2446), G3 (28; 194 +/- 1376), and G4 (28; 207 +/- 2234), which were statistically similar. The brushing time used in the present study probably wore the CO2-lased enamel, so demineralization could not be prevented in the brushed group. (C) 2013 Society of Photo-Optical Instrumentation Engineers (SPIE) (AU)

Processo FAPESP: 03/13489-6 - Caracterização de tecidos dentais duros após irradiação laser e tratamento químico: avaliação da composição, estrutura e resistência química
Beneficiário:Luciano Bachmann
Linha de fomento: Auxílio à Pesquisa - Apoio a Jovens Pesquisadores
Processo FAPESP: 10/06861-0 - Influência da irradiação dos lasers Nd:YAG e CO2 na composição química e ultra-estrutural do esmalte dental
Beneficiário:Alessandra Marques Corrêa Afonso
Linha de fomento: Bolsas no Brasil - Pós-Doutorado
Processo FAPESP: 12/02460-6 - Espectroscopia vibracional de tecidos biológicos: diagnóstico de lesões cancerosas e caracterização química de tecidos dentais irradiados com lasers
Beneficiário:Luciano Bachmann
Linha de fomento: Auxílio à Pesquisa - Regular