Frequency of Application of AmF/NaF/SnCl2 Solution and Its Potential in Inhibiting the Progression of Erosion in Human Dental Enamel - An In Vitro Study

Autor(es)

da Silva, Camilla Vieira ^[1] ; Nazello, Jessica Laporta ^[1] ; de Freitas, Patricia Moreira ^[1]

Afiliação do(s) autor(es)

^[1] Univ Sao Paulo, Fac Dent, Dept Restorat Dent, Sao Paulo, SP - Brazil

• Tipo de documento: Artigo Científico
• Fonte: ORAL HEALTH & PREVENTIVE DENTISTRY; v. 15, n. 4, p. 365-370, SEP 1 2017.
• Citações Web of Science: 0

Resumo

Purpose: To evaluate whether increasing the frequency of its use can enhance the protective effect of AmF/NaF/SnCl2 solution against dental erosion. Materials and Methods: Sixty human enamel samples were obtained from sound human third molars, and after the formation of incipient erosive lesions (1% citric acid, pH 4.0, for 3 min), they were divided into five treatment groups (n = 12): G1-deionised water (negative control); G2-NaF solution (positive control) once a day; G3-NaF solution (positive control) twice a day; G4-AmF/NaF/SnCl2 solution once a day; G5-AmF/NaF/SnCl2 solution twice a day. The samples were then subjected to 5 days of erosive cycling through 6 daily immersions (2 min each) in citric acid solution (0.05 M, pH 2.6). At the end of erosive cycling, surface wear was determined by means of optical profilometry. Results: One-way ANOVA showed that the surface wear was affected by surface treatments (p < 0.001). Tukey's test showed no difference between the groups in which NaF was applied once or twice, but they showed limited reduction in wear compared to the deionised water group (G1). In the groups treated with the AmF/NaF/SnCl2 solution, there was a statistically significant difference between one and two application times (p < 0.001). Although both demonstrated statistically significantly reduced tissue loss, increasing the frequency increased its anti-erosive potential. Conclusion: The AmF/NaF/SnCl2 solution proved to be effective in reducing dental enamel surface loss and its use twice a day potentiated its anti-erosive effect. (AU)

• Processo FAPESP: 14/25514-0 - Avaliação in vitro do potencial da solução de AmF/NaF/SnCl2 em inibir a progressão da lesão de erosão no esmalte dental humano
• Beneficiário: Jéssica Laporta Nazello
• Linha de fomento: Bolsas no Brasil - Iniciação Científica
• Processo FAPESP: 14/10955-0 - Avaliação in situ do potencial do SnF2 em inibir a progressão do processo de erosão no esmalte dental humano
• Beneficiário: Camila Vieira da Silva
• Linha de fomento: Bolsas no Brasil - Mestrado