Effect of unequal levels of deformation and fragmentation on the electrochemical response of friction stir welded AA2024-T3 alloy

Autor(es):Mostrar menos -

Queiroz, Fernanda Martins ^[1] ; Donatus, Uyime ^[2] ; Prada Ramirez, Oscar Mauricio ^[1] ; de Sousa Araujo, Joao Victor ^[2] ; Goncalves de Viveiros, Barbara Victoria ^[2] ; Lamaka, Sviatlana ^[3] ; Zheludkevich, Mikhail ^[3] ; Masoumi, Mohammad ^[4] ; Vivier, Vincent ^[5] ; Costa, Isolda ^[2] ; de Melo, Hercilio Gomes ^[1]

Afiliação do(s) autor(es)

^[1] EPUSP, PMT, Dept Engn Met & Mat, Av Prof Mello Moraes 2463, Sao Paulo, SP - Brazil

^[2] IPEN, CCTM, Av Prof Lineu Prestes 2242, Sao Paulo, SP - Brazil

^[3] HZG, MagIC, Inst Mat Res, Magnesium Innovat Ctr, Max Planck Str 1, D-21502 Geesthacht - Germany

^[4] Univ Fed ABC, UFABC, CECS, Ctr Engn Modelagem & Ciencias Sociais Aplicadas, Ave Estados 5001, Santo Andre, SP - Brazil

^[5] Sorbonne Univ, CNRS, F-75005 Paris - France

• Tipo de documento: Artigo Científico
• Fonte: Electrochimica Acta; v. 313, p. 271-281, AUG 1 2019.
• Citações Web of Science: 1

Resumo

The effect of unequal levels of deformation and fragmentation on the electrochemical response of friction stir welded AA2024-T3 has been investigated using electron backscatter diffraction, scanning electron microscopy, global and localized electrochemical techniques. The friction stir welding process introduced unequal distribution and fragmentation of coarse intermetallic particles, such that more clusters of these particles were present in the thermomechanically affected zone of the weld. This resulted in a higher susceptibility to severe localized corrosion in this region when compared with the others. Results from electrochemical measurements using a microcell could not be clearly correlated with the corrosion behaviour because no significant differences were observed using these techniques. On the other hand, LEIS and SVET results were in agreement and correlated with the corrosion evolution at the surfaces of the tested samples. (C) 2019 Elsevier Ltd. All rights reserved. (AU)

• Processo FAPESP: 13/13235-6 - Estudo da corrosão localizada e caracterização da resistência à corrosão associada à fadiga na região de solda em ligas de alumínio de elevada resistência soldadas por fricção (FSW)
• Beneficiário: Isolda Costa
• Modalidade de apoio: Auxílio à Pesquisa - Temático
• Processo FAPESP: 17/03095-3 - Investigação da suscetibilidade à corrosão de ligas Al-Cu-Li com solda por atrito (FSW) utilizando a técnica de varredura do eletrodo vibratório (SVET)
• Beneficiário: Uyime Donatus
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado
• Processo FAPESP: 16/20572-7 - Uso da espectroscopia de impedância local (LEIS) para estudo da corrosão de ligas de alumínio de elevada resistência mecânica soldadas por FSW
• Beneficiário: Fernanda Martins Queiroz
• Modalidade de apoio: Bolsas no Brasil - Pós-Doutorado