In vitro evaluation of erbium, chromium:yttrium-scandium-gallium-garnet laser-treated enamel demineralization

Texto completo
Autor(es):
de Freitas, Patricia M. [1] ; Rapozo-Hilo, Marcia [2] ; Eduardo, Carlos de P. [1] ; Featherstone, John D. B. [2]
Número total de Autores: 4
Afiliação do(s) autor(es):
[1] Univ Sao Paulo, Dept Restorat Dent, Sch Dent, BR-05508900 Sao Paulo - Brazil
[2] Univ Calif San Francisco, Dept Prevent & Restorat Dent Sci, San Francisco, CA 94143 - USA
Número total de Afiliações: 2
Tipo de documento: Artigo Científico
Fonte: Lasers in Medical Science; v. 25, n. 2, p. 165-170, MAR 2010.
Citações Web of Science: 26
Resumo

This study evaluated the effect of different parameters of erbium, chromium:yttrium-scandium-gallium-garnet (Er,Cr:YSGG) laser irradiation on enamel mineral loss in a simulated caries model. Forty-five enamel samples obtained from third molar teeth (3 mmx 3 mm) were randomly divided into five groups (n = 9): G1-Er,Cr:YSGG laser at 0.25 W, 20 Hz, 2.8 J/cm(2); G2-Er,Cr:YSGG laser at 0.50 W, 20 Hz, 5.7 J/cm(2); G3-Er,Cr:YSGG laser at 0.75 W, 20 Hz, 8.5 J/cm(2); G4-sodium fluoride (NaF) dentifrice (positive control); G5-no treatment (negative control). After irradiation, the samples were submitted to 2 weeks of pH cycling. After the acid challenge, the samples were assessed by cross-sectional microhardness at different depths from the enamel surface. Analysis of variance (ANOVA) and Student-Newman-Keuls tests were performed (alpha = 5%). The percentage of lesion inhibition for each group was: G1 37%; G2 38%; G3 64%, and G4 50.5%. Regarding the relative mineral loss values (micrometers x volume percent), groups G1 (1,392 +/- 522) and G2 (1,292 +/- 657) did not differ significantly from each other, but both had higher values than group G3 (753 +/- 287); the groups irradiated with Er,Cr:YSGG laser did not differ from group G4. Although the findings of the study revealed that Er,Cr:YSGG laser irradiation at 8.5 J/cm(2) can be an alternative for the enhancement of the enamel's resistance to acid, lower energy densities also produced a cariostatic potential comparable to the use of fluoride dentifrice. (AU)

Processo FAPESP: 03/10000-6 - Estudo in vitro do efeito da radiação do laser de Er, Cr:YSGG na inibição do processo de desmineralização e incorporação de flúor no esmalte dental
Beneficiário:Patricia Moreira de Freitas Costa e Silva
Modalidade de apoio: Bolsas no Brasil - Doutorado
Processo FAPESP: 04/12314-0 - Estudo in vitro do efeito da radiação do laser de Er, Cr:YSGG na inibição do processo de desmineralização e incorporação de flúor no esmalte dental
Beneficiário:Carlos de Paula Eduardo
Modalidade de apoio: Auxílio à Pesquisa - Regular
Processo FAPESP: 98/14270-8 - Centro de Ciências Ópticas e Fotônica
Beneficiário:Vanderlei Salvador Bagnato
Modalidade de apoio: Auxílio à Pesquisa - Centros de Pesquisa, Inovação e Difusão - CEPIDs