Effect of home-bleaching gels modified by calcium and/or fluoride and the application of nano-hydroxyapatite paste on in vitro enamel erosion susceptibility

Autor(es)

Thives Freitas Santos, Luciana Floriani ^[1] ; Gomes Torres, Carlos Rocha ^[1] ; Ferraz Caneppele, Taciana Marco ^[1] ; Magalhaes, Carolina ^[2] ; Borges, Alessandra Buhler ^[1]

Afiliação do(s) autor(es)

^[1] Univ Estadual Paulista, UNESP, Inst Sci & Technol, Dept Restorat Dent, BR-12245000 Sao Jose Dos Campos, SP - Brazil

^[2] Univ Sao Paulo, Bauru Sch Dent, Dept Biol Sci, Bauru, SP - Brazil

• Tipo de documento: Artigo Científico
• Fonte: ACTA ODONTOLOGICA SCANDINAVICA; v. 74, n. 2, p. 121-126, FEB 17 2016.
• Citações Web of Science: 8

Resumo

Objective. This in vitro study compared the effect of bleaching agents modified by the addition of calcium and/or fluoride and the application of a nano-hydroxyapatite paste after bleaching, on the susceptibility of enamel to erosion. Materials and methods. Bovine enamel cylindrical samples (3 mm diameter) were assigned to six groups (n = 20 specimens/group) according to the bleaching agent: no bleaching (C-control), 7.5% hydrogen peroxide gel (HP), HP with 0.5% calcium gluconate (HP+Ca), HP with 0.2% sodium fluoride (HP+F), HP with calcium and fluoride (HP+Ca+F) and HP followed by the application of a nano-hydroxyapatite agent (HP+NanoP). The gels were applied on the enamel surface (1 h) followed by cyclic erosive challenges (Sprite Zero (R)-2 min), for 14 days. The paste was applied after bleaching for 5 min (HP+NanoP). The enamel surface alteration was measured by contact profilometry (mu m) (after 7 and 14 days). Results. C-control (mean +/- SD: 2.29 +/- 0.37 at 7 days/4.86 +/- 0.72 at 14 days) showed significantly lower loss compared to the experimental groups. HP+Ca (3.34 +/- 0.37/6.75 +/- 1.09) and HP+F (4.49 +/- 0.92/7.61 +/- 0.90) presented significantly lower enamel loss than HP (4.18 +/- 0.50/10.30 +/- 1.58) only for 14 days and HP+Ca+F (4.92 +/- 1.03/8.12 +/- 1.52) showed values similar to the HP+F group. The HP+NanoP (5.51 +/- 1.04/9.61 +/- 1.21) resulted in enamel loss similar to the HP after 14 days. Conclusions. It was found that 7.5% hydrogen peroxide increased the susceptibility of enamel to erosion. The addition of calcium or fluoride to the bleaching gel reduced the erosion effect, while the nano-hydroxyapatite agent did not provide any protective effect. (AU)