| Abstract | |
Recently in Brazil there has been constant investments in ethanol plants, to supply the internal and external market, resulting at a high increase of the volume of this product. However, economical and environmental problems arose because of this new demand, whereas the current technologies produce thirteen liters of vinasse for each liter of alcohol. Each ECOVIN uses nearly 4000 welded tubes in the heat exchangers, and there is an option to use welded AISI 444 alloy tubes in order to reduce the manufacture costs of the ECOVIN. In this context, this work determines the corrosion mechanisms and analyzes the performance of welded tubes and the tube-to-tubesheet welded joints. The following types of tube-to-tubesheet were evaluated: current welded joints of this project, with all components manufactured with AISI 316L alloy; and the welded joint suggested for the project, using the welded tubes of AISI 444 alloy and the plate of AISI 316L alloy. For this purpose, the first step was to evaluate the weldability of the studied alloys, through microstructural characterization, welding procedure qualification and the intergranular corrosion test. After that, mass loss tests were conducted in 0,5 M \'H IND.2\'SO IND.4\' and 0,5 M \'H\'CL\' solutions, at 30°C, 50°C, 70°C and 90°C, according to the temperature range of the equipment operating. Electrochemical polarization tests were made in the same solution concentration used in the mass loss tests, but only in room temperature. These tests were made in samples that were welded with the same thermal cycle of the tube-to-tubesheet welded joints, and the evaluations were made on the base metal, heat affected zones and weld metal. The uniform and localized corrosion process occurred preferentially in the interface formed between tube and weld metal, and on weld metal near the tubes. In the tube-to-tubesheet dissimilar welded joints, it was observed that the corrosion process was predominant on the surface of AISI 444 alloy, probably because of the galvanic corrosion process, where the AISI 444 was an anodic region. The best performance on corrosion process was observed in AISI 316L, both the base metal and the similar welded joints. However, for the tests in chloride environment, in this process, the temperature caused a proportional influence in the corrosion rate of AISI 316L and AISI 444. In the AISI 316L alloy it was observed nucleation of pitting in HAZ and in weld metal, in both solutions, and more aggressive than observed in the AISI 444 alloy. The results showed that the AISI 444 alloy can be applied for the initial ranging temperatures of the equipments operation, with satisfactory performance. (AU) | |
| FAPESP's process: | 10/04586-1 - Corrosion performance analysis of tube-to-tubesheet welded joints formed by austenitic 316L and ferritic 444 stainless steels used in heat exchangers |