Effect of shrinkage compensating and reducing admixtures in alkali activated slag mortars and pastes.

Author(s)

Antônio Acacio de Melo Neto

• Document type: Doctoral Thesis
• Press: São Paulo.
• Institution: Universidade de São Paulo (USP). Escola Politécnica (EP/BC)
• Defense date: 2007-12-11

Examining board members

Maria Alba Cincotto; Antonio Domingues de Figueiredo; Geraldo Cechella Isaia; Vanderley Moacyr John; Wellington Longuini Repette

• Advisor: Maria Alba Cincotto

Abstract

The aim of this research was the study of the influence of shrinkage reducing admixture (SRA) and shrinkage compensating admixture (SCA) in mortars and pastes of blast furnace slag activated with sodium silicate. The method was centered in the analysis of free drying and autogenous shrinkage, with other characteristics that affect the shrinkage, as the mechanical properties. The microstructure behavior was accomplished with thermogravimetry (TG), mercury intrusion porosimetry (MIP) and X-ray diffraction (XRD). The samples were prepared with 0,5%, 1%, 1,5% and 2% of SRA admixture and 5%, 10% and 15% of SCA admixture, by binder mass. The effect of water/binder ratio was accomplished in three contents: 0,40, 0,48 and 0,56. In the reference mixtures, without admixtures, it was observed that an increase of water/binder ratio incurs in an increase of drying and autogenous shrinkage of alkali activated slag. The explanations for drying shrinkage behavior are the decrease of mechanical strength as consequence of water/binder increase, that turns the porous structure more susceptible to deformations, and the increase of the capillary tensions, attributed to the increase of free water to be evaporated. The increase of autogenous shrinkage with water/binder ratio is attributed to the increase of pore volume with diameter in the mesopores range, besides the decrease of the mechanical strength. The shrinkage reducing admixture (SRA) diminish drying shrinkage of 40% up to 74% at 28 days, however, this type of admixture was not capable to combat the autogenous shrinkage. About mechanical strength, the SRA admixture incurs in a decrease up to 40% of compression strength that it was attributed to the decrease of the hydration degree and retard of pore size refinement. The shrinkage compensating admixture (SCA) softened drying and autogenous shrinkage, reducing in up to 64% and 70%, respectively. However, the SCA admixture decreases in up to 60% mechanical strength of alkali activated slag. About microstructure, SCA admixture reduced the hydration degree and it increased the total porosity, with the increase of macropores volume. (AU)