Combined effects of SiO2 ratio and purity on physical properties and microstructure of in situ alumina-mullite ceramic

Full text
Author(s):
Salomao, Rafael [1] ; Fernandes, Leandro [2, 1] ; Spera, Natalia C. M. [1, 3]
Total Authors: 3
Affiliation:
[1] Univ Sao Paulo, Sao Carlos Sch Engn, Mat Engn Dept, Ave Trabalhador Saocarlense 400, Sao Carlos - Brazil
[2] Sao Paulo State Univ UNESP, Sch Dent, Dept Dent Mat & Prosthodont, Araraquara, SP - Brazil
[3] Int Iberian Nanotechnol Lab INL, Braga - Portugal
Total Affiliations: 3
Document type: Journal article
Source: International Journal of Applied Ceramic Technology; v. 18, n. 5, p. 1702-1709, SEP 2021.
Web of Science Citations: 1
Abstract

The in situ formation of mullite (Al6Si4O13) is a complex process based on solid-state reactions strongly affected by the characteristics of Al2O3 and SiO2 sources. This study investigated the combined effects of variable SiO2/Al2O3 ratios and the presence of low-melting-point impurities on the physical properties and microstructure of in situ alumina-mullite ceramics. Two grades of synthetic amorphous silica, known as microsilica, of similar physical properties and significant differences in the content of alkali-based impurities (0.8 and 3.6 wt%), were combined with thin calcined alumina particles in different proportions (from silica-free up to stoichiometric mullite), pressed and sintered. The samples were tested for total porosity, flexural strength, and pore size distribution, and their crystalline phases and microstructures formed were investigated. Small amounts of both microsilica grades (up to 8.9 wt%) hindered the densification of the alumina-mullite matrix and favored grain growth events, increasing porosity and reducing strength. For samples containing higher microsilica loads (16.4-28.2 wt%), the impurities content significantly affected the amount of liquid phases formed. Such impurities altered the ratio and shape of the pores and the total amount of mullite after sintering. Therefore, different microstructures and levels of flexural strength and total porosity were observed. (AU)