The Influence of Implant Design Features on the Bone Healing Pathway: An Experimental Study in Sheep

Author(s)

Bergamo, Edmara T. P. ; de Oliveira, Paula G. F. P. ; Jimbo, Ryo ; Neiva, Rodrigo ; Gil, Luiz F. ; Tovar, Nick ; Wtek, Lukasz ; Bonfante, Estevam A. ; Coelho, Paulo G.

• Document type: Journal article
• Source: INTERNATIONAL JOURNAL OF PERIODONTICS & RESTORATIVE DENTISTRY; v. 43, n. 3, p. 8-pg., 2023-05-01.

Abstract

This study evaluated how implant design features influence osseointegration. Two implant macrogeometries and surface treatments were evaluated: (1) progressive buttress threads with an SLActive surface (SLActive/BL), and (2) inner and outer trapezoidal threads with a nanohydroxyapatite coating over a dual acid-etched surface (Nano/U). Implants were placed in the right ilium of 12 sheep, and histologic and-metric analyses were conducted after 12 weeks. Percentages of bone-to-implant contact (BIC) and bone area fraction occupancy (BAFO) within the threads were quantified. Histologically, the SLActive/BL group showed greater and more intimate BIC than the Nano/U group. In contrast, Nano/U group depicted woven bone formation within the healing chambers, between the osteotomy wall and implant threads, and bone remodeling was evident at the outer thread tip. Significantly higher BAFO was seen in the Nano/U group than the SLActive/BL group at 12 weeks (P < .042). Different implant design features influenced the osseointegration pathway, supporting further investigations to describe the differences and clinical performance. Int J Periodontics Restorative Dent 2023;43:337-343. doi: 10.11607/prd.5438 (AU)

• FAPESP's process: 12/19078-7 - Development and processing of Al2O3-ZrO2 translucent composite for CAD/CAM monolithic prostheses: the effect of aging on biaxial flexural strength
• Grantee: Estevam Augusto Bonfante
• Support Opportunities: Research Grants - Young Investigators Grants
• FAPESP's process: 21/06730-7 - Towards sustainable zirconia recycled from milling waste and boosted by glass infiltration for restorative use, and of the development of strong, graded, and aging resistant multilayered zirconia blocks
• Grantee: Estevam Augusto Bonfante
• Support Opportunities: Research Grants - Young Investigators Grants - Phase 2
• FAPESP's process: 19/08693-1 - Experimental glass-infiltrated alumina-zirconia composites: characterization of microstructure, optical and mechanical properties.
• Grantee: Edmara Tatiely Pedroso Bergamo
• Support Opportunities: Scholarships in Brazil - Post-Doctoral