Comparison of performance of AISI 4340, 4140, 5140 and 300M steels nitrited by plasma in different conditions

Author(s)

Marcus Alberto Della Coletta

• Document type: Master's Dissertation
• Press: São Carlos.
• Institution: Universidade de São Paulo (USP). Instituto de Física de São Carlos (IFSC/BT)
• Defense date: 2000-09-22

Examining board members

Luiz Carlos Casteletti; Claudemiro Bolfarini; Tomaz Toshimi Ishikawa

• Advisor: Luiz Carlos Casteletti

Abstract

The ultrahigh-strength steels with medium carbon and low alloy, like AISI 4340, show excellent tensile strength and fatigue properties further higher hardenability. However, these steels have the phenomenon of tempering embrittlement, that restrict the temperature of treatments after quench or surfaces treatments. The 300M steel was developed aiming the enlargement this area of application, this steel permits treatments in temperatures about 350°C what allowed to use the plasma nitriding without problems with the embrittlement. In this production were compared the properties of the nitrited layers of the 300M nitriding by plasma in 350°C and 550°C with the steels AISI 4340, AISI 4140, AISI 5140 nitriding in 550°C. Plasma nitriding conditions like time and pulse frequency were varied. It was checked that the plasma nitriding showed good performance to improve the resistance to the abrasive wear in ali the steels tested. The 300M steel nitrited in 350°C showed results similar to the others in the pin-on-disk test and the better result occurred to the 300M steel nitrited in 550°C in dC plasma during 6 hours, because of a duble compound lawyer that arouse with a high thickness and high hardness. (AU)