Mass and Surface Fractal in Supercritical Dried Silica Aerogels Prepared with Additions of Sodium Dodecyl Sulfate

Author(s)

Perissinotto, Amanda P. ^[1] ; Awano, Carlos M. ^[1] ; Donatti, Dario A. ^[1] ; de Vicente, Fabio S. ^[1] ; Vollet, Dimas R. ^[1]

Affiliation

^[1] Unesp Univ Estadual Paulista, Dept Fis, IGCE, BR-13500970 Rio Claro, SP - Brazil

• Document type: Journal article
• Source: Langmuir; v. 31, n. 1, p. 562-568, JAN 13 2015.
• Web of Science Citations: 10

Abstract

Silica wet gels were prepared from hydrolysis of tetraethoxysilane (TEOS) with additions of sodium dodecyl sulfate (SDS). The surfactant was removed after gelation. Wet gels exhibited mass-fractal structure with mass-fractal dimension D (typically around 2.25) in a length scale extending from a characteristic size xi (typically about 10 nm) of the mass-fractal domains to a characteristic size a(0) (typically between 0.3 and 0.4 nm) of the primary particles building up the fractal domains. xi increased while D and a(0) diminished slightly as the SDS quantity increased. Aerogels with typical specific surface of 1000 m(2)/g and density of 0.20 g/cm(3) were obtained by supercritical drying of the wet gels after washing with ethanol and n-hexane. The pore volume and the mean pore size increased with the increase of the SDS quantity. The aerogels presented most of the mass-fractal characteristics of the original wet gels at large length scales and exhibited at a higher resolution level at about 0.7 nm a crossover to a mass-surface fractal structure, with apparent mass-fractal dimension D-m similar to 2.4 and surface-fractal dimension D-s similar to 2.6, as inferred from small-angle X-ray scattering (SAXS) and nitrogen adsorption data. (AU)

• FAPESP's process: 11/18149-5 - Study of Photosensitivity and photoluminescence in organically modified silicates films prepared by sol-gel
• Grantee: Fábio Simões de Vicente
• Support Opportunities: Regular Research Grants