Synthesis and characterization of polyarylacetylene for use in the monolithic vitreous carbon processing

Full text
Author(s):
Silvia Sizuka Oishi [1] ; Edson Cocchieri Botelho [2] ; Christine Keiko Luscombe [3] ; Mirabel Cerqueira Rezende [4]
Total Authors: 4
Affiliation:
[1] Universidade Estadual Paulista. Faculdade de Engenharia de Guaratinguetá
[2] Universidade Estadual Paulista. Faculdade de Engenharia de Guaratinguetá
[3] University of Washington. Department of Materials Science and Engineering
[4] Universidade Federal de São Paulo. Instituto de Ciência e Tecnologia
Total Affiliations: 4
Document type: Journal article
Source: POLIMEROS-CIENCIA E TECNOLOGIA; v. 24, n. 5, p. 541-546, 2014-09-22.
Abstract

In this work, polyarylacetylene (PAA) prepolymer obtained from 1,4-diethynylbenzene was evaluated as polymeric precursor of monolithic vitreous carbon (MVC). The monomer 1,4-diethynylbenzene was synthesized and the PAA prepolymer was prepared with 13, 16 and 19 wt % of nickel catalyst. The best percentage of nickel catalyst considered was 13 wt %, due to the lower molecular weight and polydispersity index and higher carbon yield. The traditional production of MVC is obtained from phenolic and poly(furfuryl alcohol) resins, which require many hours to pyrolyze due to the large quantity of gases generated. Furthermore, the porosity is hard to control using these conventional resins. Polyarylacetylene releases little volatiles due to the polyaddition reaction and the aromatic rings in PAA chain also provide a high thermal stability, therefore the heat treatment could be faster without cracking the carbon material. This would also lower the cost of fabrication of MVC, in addition to the low porosity observed, making this polymer a good matrix for MVC. (AU)

FAPESP's process: 11/23480-2 - Synthesis and characterization of polyarylacetylene resin for use in monolithic vitreous carbon processing
Grantee:Silvia Sizuka Oishi
Support Opportunities: Scholarships abroad - Research Internship - Doctorate
FAPESP's process: 11/05908-5 - Production and characterization of monolithic vitreous carbon starting by using polyarylacetylene and furfuryl alcohol resins
Grantee:Silvia Sizuka Oishi
Support Opportunities: Scholarships in Brazil - Doctorate