Room-temperature multiferroic behavior in the three-layer Aurivillius compound Bi3.25La0.75Ti2Nb0.5(Fe1-x Co-x)(0.5)O-12

Author(s)

Lavado, C. ; Alkathy, Mahmoud. S. ; Eiras, J. A. ; Stachiotti, M. G.

• Document type: Journal article
• Source: APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING; v. 129, n. 2, p. 10-pg., 2023-02-01.

Abstract

Multiferroic Bi3.25La0.75Ti2Nb0.5(Fe1-xCox)(0.5)O-12 ceramics with x = 0, 0.3, 0.4 and 0.5 were synthesized by a conventional solid-state reaction route to evaluate the effects of cobalt doping on structural, electrical and magnetic properties. All samples display layered perovskite Aurivillius phase with typical microstructure of plate-like grains. The grain size decreases with increasing Co content, from similar to 5 mu m to similar to 1 mu m. Room-temperature dielectric permittivity values range from 160 (x = 0) to 210 (x = 0.5) with negligible frequency dispersion and losses below 0.02 in a wide frequency range. A decrease of the Curie temperature with Co addition was observed. The Co-doped ceramics display well-defined ferroelectric and ferromagnetic hysteresis loops at room temperature. The best magnetic properties are obtained for x = 0.3 and x = 0.4 with a remnant magnetization of similar to 0.1 emu/g. Butterfly-type hysteresis loops are observed for the magnetodielectric response using a measurement protocol that can be useful for other single-phase multiferroic materials. The MD coefficient does not depend on frequency and the maximum value (similar to 0.5%) is obtained for cobalt content x = 0.3. So, these multiferroic three-layer Aurivillius compounds may be considered as promising candidates for memory applications. (AU)

• FAPESP's process: 19/03110-8 - Synthesis and photovoltaic characterization of thin films based on ferroelectric and multiferroic perovskite for solar cells application
• Grantee: Mahmoud Saleh Mohammed Alkathy
• Support Opportunities: Scholarships in Brazil - Post-Doctoral
• FAPESP's process: 17/13769-1 - Multiferroic and ferroelectric materials for energy converters: synthesis, properties, phenomenology and applications
• Grantee: José Antonio Eiras
• Support Opportunities: Research Projects - Thematic Grants