Fracture toughness of duplex CrN/DLC and nano-multilayer DLC-W deposited on valve tappet via hybrid PVD and PECVD

Full text
Author(s):
Kolawole, Funsho Olaitan ; Kolawole, Shola Kolade ; Bello, Sefiu Adekunle ; Yakubu, Shedrach ; Adigun, Oluwole Daniel ; Owa, Adebayo Felix ; Umunakwe, Reginald ; Adebayo, Abdullahi Olawale ; Madueke, Chioma Ifeyinwa
Total Authors: 9
Document type: Journal article
Source: SADHANA-ACADEMY PROCEEDINGS IN ENGINEERING SCIENCES; v. 49, n. 2, p. 10-pg., 2024-04-04.
Abstract

DLC coatings are well known for their high fracture toughness, however, often exhibit poor adhesion properties on metallic substrates. The use of interlayers and metallic doping can be used to overcome such challenge. In this study duplex CrN/DLC and nano-multilayer DLC-W coatings were both deposited on hydraulic valve tappet using a hybrid PVD/PECVD deposition system. Microhardness measurements were taken for the uncoated valve tappet, duplex CrN/DLC and nano-multilayer DLC-W coated valve tappet at loads of 0.98 N, 1.96 N, 2.94 N, 4.9 N, 9.8 N and 19.6 N for 15 seconds using a Shimadzu hardness tester. The fracture toughness was evaluated using the Vickers indentation method from microhardness indents on the surface of the coatings. The fracture toughness for duplex CrN/DLC and nano-multilayer DLC-W coatings indented at 4.9 N, 9.8 N and 19.6 N, reveals that the fracture toughness for the duplex CrN/DLC were 20.24 +/- 0.97 MPa.m1/2, 17.18 +/- 0.86 MPa.m1/2 and 6.6 +/- 0.28 MPa.m1/2 respectively. While the fracture toughness for nano-multilayer DLC-W was calculated as 3.75 +/- 0.41 MPa.m1/2 and 4.67 +/- 0.38 MPa.m1/2 at 9.8 N and 19.6 N respectively. (AU)

FAPESP's process: 23/08065-6 - Studies of the effects of the nano particles incorporation in very thick DLC films
Grantee:Funsho Olaitan Kolawole
Support Opportunities: Scholarships in Brazil - Post-Doctoral
FAPESP's process: 22/05578-0 - Growth of multiferroic single crystals and characterization of optical properties for piezophotonic applications
Grantee:Yakubu Shedrach
Support Opportunities: Scholarships in Brazil - Doctorate (Direct)