Stability of fatigued and aged ZTA compared to 3Y-TZP and Al2O3 ceramic systems

Author(s):Show less -

Jalkh, Ernesto B. Benalcazar ; Bergamo, Edmara T. P. ; Campos, Tiago M. B. ; de Araujo-Junior, Everardo N. S. ; Lopes, Adolfo C. O. ; Tebcherani, Sergio M. ; Yamaguchi, Satoshi ; Genova, Luis A. ; Gierthmuehlen, Petra C. ; Witek, Lukasz ; Coelho, Paulo G. ; Bonfante, Estevam A.

• Document type: Journal article
• Source: JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS; v. 135, p. 9-pg., 2022-11-01.

Abstract

To evaluate the effect of fatigue and aging on the crystalline content and reliability of a zirconia-toughened-alumina (ZTA) composite compared to its individual counterpart materials (3Y-TZP and Al2O3).Thirty-six disc-shaped specimens per group were obtained to comply with ISO 6872:2015. Crystalline content, microstructure and reliability of experimental groups were evaluated in four stages: 1) immediate; 2) aged; 3) fatigued; 4) aged + fatigue. Aging was performed in autoclave and Step-Stress-Accelerated-Life-Testing (SSALT) was performed using three stress profiles. Weibull statistics were used to determine Weibull parameters and life -expectancy. A significant increase in monoclinic phase in 3Y-TZP was observed after aging (19.31%), fatigue (17.88%) and aging + fatigue (55.81%), while ZTA evidenced minimal variation among all conditions (<5.69%). 3Y-TZP presented higher reliability than ZTA at 300 and 500 MPa, and ZTA outperformed Al2O3 at the same stress missions. None of the ceramics yielded acceptable reliability at 800 MPa. A higher characteristic strength was observed for 3Y-TZP, followed by ZTA and Al2O3. While after aging ZTA and Al2O3 remained stable, 3Y-TZP exhibited a significant increase in the characteristic stress. Aging did not affect the reliability of ZTA and Al2O3. 3Y-TZP demonstrated an increase in monoclinic content and characteristic strength after aging. (AU)

• FAPESP's process: 19/08693-1 - Experimental glass-infiltrated alumina-zirconia composites: characterization of microstructure, optical and mechanical properties.
• Grantee: Edmara Tatiely Pedroso Bergamo
• Support Opportunities: Scholarships in Brazil - Post-Doctoral
• FAPESP's process: 17/19362-0 - DEVELOPMENT, MECHANICAL AND OPTICAL CHARACTERIZATION OF 80% AL2O3 AND 20% ZRO2 ZTA COMPOSITES FOR CAD/CAM PROSTHESES
• Grantee: Adolfo Coelho de Oliveira Lopes
• Support Opportunities: Scholarships abroad - Research Internship - Master's degree
• FAPESP's process: 21/06730-7 - Towards sustainable zirconia recycled from milling waste and boosted by glass infiltration for restorative use, and of the development of strong, graded, and aging resistant multilayered zirconia blocks
• Grantee: Estevam Augusto Bonfante
• Support Opportunities: Research Grants - Young Investigators Grants - Phase 2
• FAPESP's process: 16/17793-1 - Development and mechanical and optical characterization of 80% Al2O3 and 20% ZrO2 translucent composites for CAD/CAM monolithic prostheses
• Grantee: Adolfo Coelho de Oliveira Lopes
• Support Opportunities: Scholarships in Brazil - Master
• FAPESP's process: 19/00452-5 - EXPERIMENTAL 70%Al2O3-30%ZrO2 ZTA COMPOSITES: MECHANICAL, ESTRUCTURAL AND TOPHOGRAPHICAL CHARACTERIZATION
• Grantee: Ernesto Byron Benalcazar Jalkh
• Support Opportunities: Scholarships abroad - Research Internship - Doctorate
• FAPESP's process: 18/03072-6 - Experimental 70% Al2O3-30% ZrO2 composites: structural characterization and survival probability before and after aging
• Grantee: Ernesto Byron Benalcazar Jalkh
• Support Opportunities: Scholarships in Brazil - Doctorate
• FAPESP's process: 12/19078-7 - Development and processing of Al2O3-ZrO2 translucent composite for CAD/CAM monolithic prostheses: the effect of aging on biaxial flexural strength
• Grantee: Estevam Augusto Bonfante
• Support Opportunities: Research Grants - Young Investigators Grants
• FAPESP's process: 16/18818-8 - Multi-User Equipment approved in grant 2012/19078-7: ElectroPuls E3000 Linear-Torsion All-Electric dynamic test instrument package
• Grantee: Estevam Augusto Bonfante
• Support Opportunities: Multi-user Equipment Program
• FAPESP's process: 21/08018-2 - Nanomechanical layer characterization of graded ATZ and ZTA composites
• Grantee: Edmara Tatiely Pedroso Bergamo
• Support Opportunities: Scholarships abroad - Research Internship - Post-doctor
• FAPESP's process: 22/07157-1 - Physical and mechanical characterization of a multilayered system using recycled zirconia
• Grantee: Ernesto Byron Benalcazar Jalkh
• Support Opportunities: Scholarships in Brazil - Post-Doctoral