The Impacts of Co and Ni Additions to High Solute Content Fe-Contaminated Al alloys in Beneficing Microstructure and Tensile Properties

Full text
Author(s):
Marcella Gautê Cavalcante Xavier [1] ; José Eduardo Spinelli [2]
Total Authors: 2
Affiliation:
[1] Universidade Federal de São Carlos. Programa de Pós-Graduação em Ciência e Engenharia de Materiais - Brasil
[2] Universidade Federal de São Carlos. Departamento de Engenharia de Materiais - Brasil
Total Affiliations: 2
Document type: Journal article
Source: MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS; v. 27, 2024-03-25.
Abstract

The accumulation of tramp impurities, particularly Fe, during recycling of Al alloys frequently leads to the production of coarse intermetallics during solidification, which affect final product mechanical properties. Because lowering the Fe concentration and/or using thermomechanical processing to subdivide the particles is expensive, it is preferred to modify the morphology, size, and distribution of the IMCs during solidification. Benefiting the properties of Al-contaminated alloys entails increased recyclability and a reduction in the usage of virgin primary Al and downcycled alloys. The Al-8%Si-0.8%Fe-2.5%Cu-1.0%Zn (in wt.%) alloy was modified with 0.7%Ni and 0.7%Co. Both dendritic growth and tensile properties were evaluated for the three alloys. The secondary dendrite arm spacing values (λ2) were found very refined for all alloys. The λ2 in the modified alloys was even more reduced. The Co addition of 0.7% reached higher values of tensile strength (220 MPa) as compared to the others without major losses in ductility. The addition of Co can enhance strength by up to 15%, considering more refined microstructures. (AU)

FAPESP's process: 19/23673-7 - Evaluation of alloys for thermal interface contact and for additive manufacturing
Grantee:José Eduardo Spinelli
Support Opportunities: Regular Research Grants
FAPESP's process: 23/06107-3 - Study of the growth of AlFe primary phases in Al alloys and of intermetallic layers in Sn-Bi-X/copper joints
Grantee:José Eduardo Spinelli
Support Opportunities: Regular Research Grants