Reliability and Failure Mode of Ti-Base Abutments Supported by Narrow/Wide Implant Systems

Author(s):Show less -

Benalcazar-Jalkh, Ernesto B. ; de Carvalho, Laura F. ; Alves, Larissa M. M. ; Campos, Tiago M. B. ; Sousa, Edisa de Oliveira ; Bergamo, Edmara T. P. ; Coelho, Paulo G. ; Gierthmuehlen, Petra C. ; Spitznagel, Frank A. ; Zahoui, Abbas ; Bonfante, Estevam A.

• Document type: Journal article
• Source: DENTISTRY JOURNAL; v. 11, n. 9, p. 11-pg., 2023-09-01.

Abstract

To assess the reliability and failure modes of Ti-base abutments supported by narrow and wide-diameter implant systems. Narrow (o3.5 x 10 mm) and wide (o5 x 10 mm) implant systems of two different manufacturers with internal conical connections (16 degrees) and their respective Ti-base abutments (3.5 and 4.5 mm) were evaluated. Ti-base abutments were torqued to the implants, standardized metallic maxillary incisor crowns were cemented, and step stress accelerated life testing of eighteen assemblies per group was performed in three loading profiles: mild, moderate, and aggressive until fracture or suspension. Reliability for missions of 100,000 cycles at 100 and 150 N was calculated, and fractographic analysis was performed. For missions at 100 N for 100,000 cycles, both narrow and wide implant systems exhibited a high probability of survival (>= 99%, CI: 94-100%) without significant differences. At 150 N, wide-diameter implants presented higher reliability (>= 99%, CI: 99-100%) compared to narrow implants (86%, CI: 61-95%), with no significant differences among manufacturers. Failure mode predominantly involved Ti-base abutment fractures at the abutment platform. Ti-base abutments supported by narrow and wide implant systems presented high reliability for physiologic masticatory forces, whereas for high load-bearing applications, wide-diameter implants presented increased reliability. Failures were confined to abutment fractures. (AU)

• FAPESP's process: 21/06730-7 - Towards sustainable zirconia recycled from milling waste and boosted by glass infiltration for restorative use, and of the development of strong, graded, and aging resistant multilayered zirconia blocks
• Grantee: Estevam Augusto Bonfante
• Support Opportunities: Research Grants - Young Investigators Grants - Phase 2
• FAPESP's process: 21/08018-2 - Nanomechanical layer characterization of graded ATZ and ZTA composites
• Grantee: Edmara Tatiely Pedroso Bergamo
• Support Opportunities: Scholarships abroad - Research Internship - Post-doctor
• FAPESP's process: 20/12874-9 - Infiltration graded by glass in an experimental composite based on whiskers of alumina and zircônia: development, microstructural characterization and optical and mechanical properties
• Grantee: Tiago Moreira Bastos Campos
• Support Opportunities: Scholarships in Brazil - Post-Doctoral
• FAPESP's process: 21/07440-2 - Graduated glass infiltration in an ultra-translucent zirconia (5Y-PSZ): synthesis, processing and characterization of physical and mechanical properties
• Grantee: Larissa Marcia Martins Alves
• Support Opportunities: Scholarships in Brazil - Post-Doctoral
• FAPESP's process: 16/18818-8 - Multi-User Equipment approved in grant 2012/19078-7: ElectroPuls E3000 Linear-Torsion All-Electric dynamic test instrument package
• Grantee: Estevam Augusto Bonfante
• Support Opportunities: Multi-user Equipment Program
• FAPESP's process: 19/08693-1 - Experimental glass-infiltrated alumina-zirconia composites: characterization of microstructure, optical and mechanical properties.
• Grantee: Edmara Tatiely Pedroso Bergamo
• Support Opportunities: Scholarships in Brazil - Post-Doctoral
• FAPESP's process: 19/00452-5 - EXPERIMENTAL 70%Al2O3-30%ZrO2 ZTA COMPOSITES: MECHANICAL, ESTRUCTURAL AND TOPHOGRAPHICAL CHARACTERIZATION
• Grantee: Ernesto Byron Benalcazar Jalkh
• Support Opportunities: Scholarships abroad - Research Internship - Doctorate
• FAPESP's process: 22/07157-1 - Physical and mechanical characterization of a multilayered system using recycled zirconia
• Grantee: Ernesto Byron Benalcazar Jalkh
• Support Opportunities: Scholarships in Brazil - Post-Doctoral
• FAPESP's process: 18/03072-6 - Experimental 70% Al2O3-30% ZrO2 composites: structural characterization and survival probability before and after aging
• Grantee: Ernesto Byron Benalcazar Jalkh
• Support Opportunities: Scholarships in Brazil - Doctorate