Effect of different thickness, techniques of application and cooling rates in the fracture resistance of veneering ceramics applied over Y-TZP coping

• Grant number: 11/13085-9
• Support Opportunities: Scholarships in Brazil - Doctorate
• Start date: January 01, 2012
• End date: February 28, 2014
• Field of knowledge: Health Sciences - Dentistry - Dental Materials
• Principal Investigator: Marco Antonio Bottino
• Grantee: Júlia Magalhães da Costa Lima
• Host Institution: Instituto de Ciência e Tecnologia (ICT). Universidade Estadual Paulista (UNESP). Campus de São José dos Campos. São José dos Campos , SP, Brazil

Abstract

This research aims to evaluate in vitro the influence of cooling rate, the application technique and the thickness of veneering ceramic on fracture resistance in all-ceramic crowns with zirconia infrastructure. It will be done 100 crowns that will be divided into 10 groups (n = 10), where 80 samples will be divided into 8 groups according to the mode of application (stratified technique and pressed technique), thickness (1 mm and 2 mm) and cooling rate (10° C/s and 50° C/s) of two types of veneering ceramic. The other 20 crowns will be done by the Rapid Layer Technology technique and will be divided into two groups according to the thickness of veneering ceramic (1 mm and 2 mm). The thickness of the zirconia infrastructure of all crowns will be 0.5 mm. All specimens shall be mechanically cycled with a load of 84 N for 2.106 cycles at a frequency of 3.4 Hz and temperature of 37ºC. The presence or absence of chipping will be determined through analysis in stereomicroscope and Scanning Electron Microscopy. Then, all specimens would be submitted to resistance test of axial compression at a speed of 0.5 mm/min. The data will be subjected to statistical analysis using STATISTIX and MINITAB programs. (AU)

Scientific publications

(References retrieved automatically from Web of Science and SciELO through information on FAPESP grants and their corresponding numbers as mentioned in the publications by the authors)

COSTA LIMA, JULIA MAGALHAES; ANAMI, LILIAN COSTA; RIPPE, MARILIA PIVETTA; DE MELO, RENATA MARQUES; BOTTINO, MARCO ANTONIO; VALERA, MARCIA CARNEIRO; MAXIMO ARAUJO, MARIA AMELIA. Surface agents' influence on the flexural strength of bilaminated ceramics. BRAZILIAN ORAL RESEARCH, v. 27, n. 4, p. 7-pg., 2013-07-01. (11/13085-9)

JULIA MAGALHÃES COSTA LIMA; ANNA KARINA FIGUEIREDO COSTA; LILIAN COSTA ANAMI; KARINA BARBOSA SOUZA; NATHALIA RAMOS DA SILVA; RENATA MARQUES DE MELO MARINHO; ALEXANDRE LUIS SOUTO BORGES; MARCO ANTONIO BOTTINO; MUTLU ÖZCAN; RODRIGO OTHÁVIO ASSUNÇÃO SOUZA. CAD-FEA modeling and fracture resistance of bilayer zirconia crowns manufactured by the rapid layer technology. Brazilian Dental Journal, v. 32, n. 3, p. 44-55, 2021-11-08. (11/13085-9)

JULIA MAGALHAES COSTA LIMA; LILIAN COSTA ANAMI; MARILIA PIVETTA RIPPE; RENATA MARQUES DE MELO; MARCO ANTONIO BOTTINO; MARCIA CARNEIRO VALERA; MARIA AMELIA MAXIMO ARAUJO. Surface agents' influence on the flexural strength of bilaminated ceramics. Brazilian Oral Research, v. 27, n. 4, p. 311-317, 2013-07-00. (11/13085-9)

Academic Publications

(References retrieved automatically from State of São Paulo Research Institutions)

LIMA, Júlia Magalhães da Costa. Efeito de diferentes espessuras, técnicas de aplicação e protocolos de resfriamento na resistência à fratura da cerâmica de cobertura aplicada sobre infraestrutura de y-tzp. 2014. Doctoral Thesis - Universidade Estadual Paulista (Unesp). Instituto de Ciência e Tecnologia. São José dos Campos São José dos Campos.